Study of the Al-Si-X system by different cooling rates and heat treatment

The solidification behavior of the Al-12.6% Si (A1), the hypereutectic Al-20%Si (A2) and the Al-20%Si-1.5% Fe-0.5%Mn (A3) (in wt. (%)) alloys, at different cooling rates is reported and discussed. The cooling rates ranged between 0.93 °C/s and 190 °C/s when cast in sand and copper wedge-shaped molds, respectively. A spheroidization heat treatment was carried out to the alloys in the as-cast condition at 540 °C for 11 hours and quench in water with a subsequent heat treatment at 170 °C for 5 hours with the purpose of improving the mechanical properties. The samples were characterized by opt...