Sintering mechanisms of partially stabilized zirconia (TZ3Y) with ZnO and Co3O4 as sintering additives

Abstract In this work, the sintering mechanisms of 3 mol% yttria-stabilized zirconia (TZ3Y) and TZ3Y containing 0.3 wt% of ZnO or Co3O4 were analyzed by determining the apparent activation energy of sintering from dilatometry data and observing the evolution of microstructure. Dilatometry test was performed at a heating rate ranging from 5 to 20 °C/min from room temperature up to 1500 °C. The main mechanism of each sintering additive for the studied samples was revealed from the variation of the sintering activation energy as a function of the relative density and scanning electron microscop...