Nanoestructura de perovskita doble La2NiMnO6 obtenido por ruta de citrato para supercapacitores

ABSTRACT In this paper, the study of double perovskite La2NiMnO6 as electrode material for supercapacitors is presented. The mixed oxide was prepared by citrate precursor route (CIT). The sample was calcined for 4 hours at 800 °C. The material was characterized by PXRD, SEM and FTIR spectroscopy. Cyclic voltammetry and galvanostatic charge/discharge measurements were used to study the capacitive behavior of the nanomaterial in alkaline and acid solutions. I/V profiles were obtained at varying the scan rates from 10 to 100 mV/s. The galvanostatic charge/discharge curves were recorded at differ...