Microstructural analysis in the Fe-30.5Mn-8.0Al-1.2C and Fe-30.5Mn-2.1Al-1.2C steels upon cold rolling

Abstract Electron backscatter diffraction (EBSD) and electron channeling contrast imaging (ECCI) were used to examine microstructural changes of the austenitic low-density Fe-30.5Mn-8.0Al-1.2C (8Al) and Fe-30.5Mn-2.1Al-1.2C (2Al) (wt.%) steels during cold rolling. As the strain increased, deformation mechanisms, such as stacking faults, slip, mechanical twinning, and shear banding were activated in both steels cold rolled up to strain of 0.69. Only slip was noted in these steels at low strain (ε=0.11) and slip dominance was detected in the 8Al steel at higher strains. Shear banding became act...