Inorganic filler content of resin-based luting agents and the color of ceramic veneers

Abstract The influence of inorganic filler content of resin-based luting agents (RBLAs) on color change (ΔE00), CIEL*a*b* (individual color coordinates), and translucency parameters (TP) of simulated ceramic laminate veneer (CLV) was investigated. RBLAs with low, intermediate, and high inorganic filler content (55%, 65%, and 75% mass fractions, respectively) were prepared. Feldspar ceramic (Vitablocs Mark II) specimens (1.2 mm × 0.8 mm, A1C shade) were bonded to simulated composite resin substrates (1.6 mm × 1.2 mm, A2D shade) using three experimental and a commercial (RelyX Veneer) RBLA (t...