Influence of pulse-delay curing on sorption and solubility of a composite resin

The purpose of this study was to evaluate the sorption and solubility of a composite resin (TPH³; Dentsply) cured with halogen light due to different storage media and curing modes. The methodology was based on the ISO 4049 standard. Two independent groups were established according to the storage time (7 days-G1; 60 days-G2). A stainless steel mould (2 mm x 8 mm Ø) was used. The selected curing modes were: I (Conventional - C): 40s - 600 mW/cm²; II (Pulse I - PD): 3 s - 200 mW/cm² + 2 min (delay) + 39 s - 600 mW/cm²; III (Pulse II): 10 s - 200 mW/cm² + 2 min (delay) + 37 s - 600 mW/cm²...