Influence of heat treatments on the microstructure and degree of sensitization of base metal and weld of AISI 430 stainless steel

ABSTRACT AISI 430 is a non-stabilized ferritic stainless steel grade with carbon content lower than 0.12%.After hot and cold rolling this material is annealed. The slow cooling after soaking at temperatures between 900oC and 1000oC promotes the formation of a high quantity of carbides and nitrides, while the rapid cooling partially suppresses the formation of these precipitates, but introduces martensite in the microstructure. Intergranular martensite can also be produced in the weld metal and in the heat affected zone (HAZ) of welds of non-stabilized ferritic stainless steels. In this work, s...