High Temperature Erosion-oxidation Resistance of Thermally Sprayed Nanostructured Cr3C2-25(Ni-20Cr) Coatings

This study reports the high temperature erosion-oxidation (E-O) behavior of conventional and nanostructured Cr3C2-25(Ni-20Cr) coatings prepared by high velocity oxygen fuel (HVOF) spraying. As-received and nanostructured Cr3C2-25(Ni-20Cr) powders with mean crystallite sizes of 145 nm and 50 nm respectively, were used to prepare 120 - 200 µm thick coatings on AISI 310 samples. The E-O behavior of the coatings prepared with the as-received (AR) and nanostructured (NS) powders was determined as weight change in a custom designed rig at room temperature, 450, 700 and 800 ºC. The Vickers microhar...