Cr3+ Doped Al2O3 Obtained by Non-Hydrolytic Sol-Gel Methodology

This paper reports the synthesis and characterization of Cr3+-doped alumina by the sol-gel non-hydrolytic methodology. The resulting sample was treated at different temperatures. X-ray diffraction revealed that the ruby phase emerged in the sample treated at 1100 ºC, which was later confirmed by absorption bands correspondent to Cr3+ ions allowed transitions at 4A2 → 4T1, 4T2, and forbidden at 4A2 → 2T1, 2E, observed by diffuse reflectance UV-Vis. The luminescence spectroscopy showed the intensity band at 694 nm in red region, characterized of the Cr3+ ion. The peaks at 702 and 705 nm cor...