Temperature Of Calcination
Mostrando 1-12 de 110 artigos, teses e dissertações.
-
1. Tailoring the properties of Y2O3 via synthesis parameters varied during the PVA-assisted sol-gel route
Abstract The effect of synthesis parameters on the microstructural behavior and morphology during the yttrium oxide (Y2O3) formation is reported. Y2O3 crystals were produced by a modified sol-gel route assisted by polyvinyl alcohol solution varying the calcination temperature and solution pH. The crystalline phase formation was investigated using X-ray powde
Cerâmica. Publicado em: 2023
-
2. Study of rhombohedral tricalcium phosphate in hexagonal crystal structure family on the sample prepared by the sol-gel route and the effect of calcination temperature
Abstract The effect of the calcination temperature at 800 and 1000 °C on the stable formation of the tricalcium phosphate with rhombohedral structure in the system of the hexagonal crystal family was determined, while its precursor was made from limestone obtained from nature in the Lumajang district, Indonesia. The rhombohedral tricalcium phosphate samples
Cerâmica. Publicado em: 2023
-
3. Analysis and evaluation of structural properties of Co3O4 microparticles obtained at low temperature
Abstract In the present research, the synthesis of cobalt oxide Co3O4 was carried out using the sol-gel technique with subsequent heat treatment at 225 and 235 °C. The final product obtained was characterized by X-ray diffraction (XRD), showing a pure crystalline phase of Co3O4, cell parameters a=b=c=8.071 Å, and a volume of 525.7 Å3. The particle size wa
Cerâmica. Publicado em: 2022
-
4. K2O SUPORTADO EM ZEÓLITA NATURAL: SÍNTESE, CARACTERIZAÇÃO E APLICAÇÃO PRODUÇÃO DE BIODIESEL A PARTIR DO ÓLEO DE GIRASSOL
Biodiesel is a renewable fuel, a substitute for fossil diesel, which is important for reducing GHG in Brazil. Therefore, this work aims to synthesize and characterize the catalyst using the support of natural zeolite impregnated with K2O and apply it in the production of biodiesel through the transesterification reaction. Through the analysis of characteriza
Química Nova. Publicado em: 2022
-
5. Thermal, structural and optical properties of magnetic BiFeO3 micron-particles synthesized by coprecipitation method: heterogeneous photocatalysis study under white LED irradiation
Abstract Bismuth ferrite, BiFeO3 (BFO) prepared via a coprecipitation method, was used as an effective photocatalyst for the degradation of methylene blue (MB) using a white light-emitting diode (LED-50 W) lamp. The as-prepared material was characterized by TGA, XRD, SEM-EDX, FTIR, and UV-vis-DRS techniques. The effects of experimental key parameters such as
Cerâmica. Publicado em: 2022
-
6. Effect of pH level and calcination on the production of calcium phosphates by acidic route of wet precipitation
Abstract Multiphasic calcium phosphate powders were synthesized by the acidic route, using lactic acid as a chelating agent that allows the production of a stable and rich solution of calcium and phosphate ions at room temperature. After pH adjusting, without varying the concentrations of precursor solution, XRD and FTIR analyses showed different CaP phases
Cerâmica. Publicado em: 2021-06
-
7. Catalytic Dehydration of Glycerol to Acrolein over Aluminum Phosphate Catalysts
Gas phase conversion of glycerol to acrolein over a variety of aluminum phosphate (AlP) catalysts synthesized by a simple replacement reaction method with a variation in calcination temperature (300-700 ºC, AlP-300, AlP-400, AlP-500, AlP-600, and AlP-700, respectively) has been investigated. The textural properties, acidities and coke contents of the sample
J. Braz. Chem. Soc.. Publicado em: 2020-08
-
8. BIODIESEL SYNTHESIS FROM WASTE COOKING OIL USING A VARIETY OF WASTE MARBLE AS HETEROGENEOUS CATALYSTS
Abstract The research article is based on biodiesel synthesis by the transesterification of waste cooking oil with methanol in the presence of heterogeneous catalysts prepared from different marble. Eight samples of marble were successfully converted into potential catalysts by calcination. The thermal treatment of waste marbles at 300oC-1000oC converted the
Braz. J. Chem. Eng.. Publicado em: 13/01/2020
-
9. SYNTHESIS OF SOLID CATALYST FROM DOLOMITE FOR BIODIESEL PRODUCTION USING PALM KERNEL OIL IN AN OPTIMIZATION PROCESS BY DEFINITIVE SCREENING DESIGN
Abstract A solid catalyst for biodiesel production was synthesized from dolomite by calcination at different temperatures of 800 and 900oC for 2 h. The catalyst was characterized by scanning electron microscopy (SEM) and Brunauer Emmett Teller (BET). Its performance in the production of palm kernel biodiesel (PKB) using palm kernel oil in an optimization stu
Braz. J. Chem. Eng.. Publicado em: 30/09/2019
-
10. Catalytic Removal of Toluene from Air Streams by Cobalt Oxide Supported on Sepiolite
Removal of toluene using cobalt oxide supported on sepiolite catalysts was investigated. Deposition precipitation method was used to prepare the catalysts. The catalysts were characterized using X-ray diffraction, field emission scanning electron microscopy, energy dispersive X-ray spectroscopy, thermogravimetric analysis (TGA) and Brunauer-Emmet-Teller meth
J. Braz. Chem. Soc.. Publicado em: 16/09/2019
-
11. Estudio de las propiedades, estructurales, morfológicas y ópticas de nanopartículas de Cr2O3 sintetizadas por procesos de combustión de un solo paso y diferentes combustibles
ABSTRACT This research presents a novel one–step solution combustion synthesis to obtain nano-structured Cr2O3 from chrome nitrate solution and one fuel such as aspartic acid (Asp) or Lysine (Lys), or Autor Restrihydroxymethylaminomethane (Tris) or ethylenediaminetetraacetic acid (Edta). Once obtained, the ashes were calcined at 500°C. The powders were ch
Matéria (Rio J.). Publicado em: 16/09/2019
-
12. CHARACTERIZATION OF SILICON-ALUMINUM-ZIRCONIUM OXIDE OBTAINED BY THE SOL-GEL PROCESS
A new silicon-aluminum-zirconium ternary oxide (SiO2/Al2O3/ZrO2) was prepared by the sol-gel method followed by one-step washing with absolute ethanol or two-step washing with absolute ethanol followed by ultra-pure water. Both ternary oxides presented high surface area (over 340 m2 g-1). The binding energy values for Zr3d and Al2p levels showed the insertio
Quím. Nova. Publicado em: 18/07/2019