Sol Gel Pechini
Mostrando 1-12 de 12 artigos, teses e dissertações.
-
1. Morphological Characterization of Tungsten Trioxide Nanopowders Synthesized by Sol-Gel Modified Pechini's Method
Sol-gel modified Pechini's method was used to prepare WO3 nanopowders using dicarboxylic acid and polyethylene glycol as the chelating agent and polymeric source, respectively. WO3 powders were first prepared by calcination of resin precursor at 550ºC under various initial concentrations of metal ion (12.5-50 mmol), acid (125-500 mmol), a complexing agent (
Mat. Res.. Publicado em: 28/09/2017
-
2. Synthesis and Structural Properties of Niobium Pentoxide Powders: A Comparative Study of the Growth Process
Powders Nb2 O5 were prepared by two different synthesis method, Sol-Gel and polymeric precursors (Pechini). In the Pechini method before adding the citric acid in the process, four different solutions were used to get the samples. For Sol-gel method, two different processes were also used in obtaining powders. The precursor was completely solubilized in etha
Mat. Res.. Publicado em: 10/10/2016
-
3. Síntese e caracterização de compostos do sistema x/2 AlO-x/2 YO (100 - x) SiO (x=10,20,30,40 e 50) dopados com Er+ para aplicação em fotônica / Synthesis and characterization of the system x/2 AlO-x/2 YO (100 - x) SiO (x=10,20,30,40 e 50) dopados com Er+ para aplicação em fotônica.
Neste trabalho estudo-se a cristalização de compostos na forma de pós do sistema alumina-ítria-sílica preparados pela metodologia mista sol-gel e Pechini. Pós de (x/2) YO-(X/2) AlO-(1-x) SiO (x=0,1 0,2, 0,3, 0,4 e 0,5 em mol) dopados com érbio foram preparados e caracterizados. As propriedades físicas dos composto de SiO-YO,5- AlO,5 foram estudadas p
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 15/12/2010
-
4. Síntese e caracterização estrutural, morfológica e óptica de partículas de PbCrO4 e Pb2CrO5 e sua dispersão em SiO2 / Synthesis and structural, morphological and optical characterization of PbCrO4 and Pb2CrO5 particles and its dispersion in SiO2
In this work, the synthesis of particles from the PbO-CrO3 system, in particular the PbCrO4 and Pb2CrO5 compositions were accomplished, by a polymeric precursor method, evaluating its application as pigments. In order to eliminate the negative toxic aspect of these materials, the dispersion of the same in SiO2 was achieved, by the sol-gel method. The samples
Publicado em: 2009
-
5. Tin and zinc oxides semiconductor devices / Dispositivos semicondutores a partir de óxidos de estanho e zinco
This work presents the study and development of semiconductor devices base on tin and zinc oxides. The first device is related to the development of pH sensors based on field effect, while the second device uses surface acoustic waves for the transport of carriers related to a single photon detector device. Initially, the semiconductors were used as hydrogen
Publicado em: 2009
-
6. Fibras monocristalinas de tungstatos duplos de metais alcalinos e terras raras: um estudo de crescimento através da técnica de micro-pulling-down / ALKALI RARE EARTH DOUBLE TUNGSTATES SINGLE CRYSTAL FIBERS: A GROWTH STUDY BY THE MICRO-PULLING DOWN METHOD
Neste trabalho, foram realizadas sínteses dos tungstatos duplos NaLa(WO4)2 (NLW), NaGd(WO4)2 (NGW) e LiLa(WO4)2 (LLW) puros e simplesmente dopados com os íons Nd3+ e Yb3+; comparando-se dois métodos de obteção: o de reação no estado sólido e o sol-gel modificado (Pechini). Verificou-se que o envelhecimento do reagente La2O3 (adsorção de umidade amb
Publicado em: 2009
-
7. Estudo analítico de rotas de síntese de dióxido de titânio / Study of synthetic routes for titanium dioxide
Amostras de titânia foram sintetizadas por seis rotas diferentes: quatro pelo método sol-gel, utilizando condições e precursores distintos, por combustão de solução líquida e pelo método Pechini. Após tratamento térmico que variou de 100°C a 900°C, as amostras foram analisadas por difratometria de raios X, termogravimetria e pelo método BET de
Publicado em: 2007
-
8. SnO2 extended gate field-effect transistor as pH sensor
Extended gate field-effect transistor (EGFET) is a device composed of a conventional ion-sensitive electrode and a MOSFET device, which can be applied to the measurement of ion content in a solution. This structure has a lot of advantages as compared to the Ion- Sensitive Field Effect Transistor (ISFET). In this work, we constructed an EGFET by connecting th
Brazilian Journal of Physics. Publicado em: 2006-06
-
9. Synthesis and characterization of Rare Earth compounds with potencial appplication in ionizing radiation detection / Síntese e caracterização de compostos de terras raras com potencial aplicação na detecção de radiação ionizante
Rare Earth (RE) inorganic phosphors play an important role as ionizing radiation detectors when applied to medical imaging techniques like radiology and tomography. These phosphors is to convert the high energy radiation absorbed photons (X or ?-rays) into visible photons, leading to better quality images and reducing the time the patient is exposed to radia
Publicado em: 2006
-
10. Preparação, caracterização e utilização de eletrodos de óxidos de níquel na eletrooxidação do furfural / Preparation, caracterization and utilization of niquel oxides eletrodes in the Furfural eletrooxidation
No presente trabalho foram preparados eletrodos formados por filmes finos de níquel e óxido de níquel sobre um substrato de Ti. Estes eletrodos foram preparados pelas metodologias de decomposição térmica de precursores poliméricos; método sol-gel e eletrodeposição com a finalidade de investigar a influência da metodologia de preparação sobre sua
Publicado em: 2006
-
11. Development of encapsulated nanometric pigments / Desenvolvimento de pigmentos nanométricos encapsulados.
No presente trabalho, pigmentos cerâmicos do tipo perovskita NiTiO3 foram preparados utilizando-se o método dos precursores poliméricos derivado do método originalmente proposto por Pechini. A resina polimérica, translúcida e viscosa, foi caracterizada usando-se análise termogravimétrica. O produto da pirólise da resina, denominado de puff, foi desa
Publicado em: 2004
-
12. Efeitos da urÃia na sÃntese de cerÃmica PZT pelo processo sol-gel.
Neste trabalho, Ã estudado o efeito da urÃia na sÃntese de PZT pelo processo sol-gel utilizando trÃs diferentes mÃtodos. No primeiro mÃtodo, chamado MÃtodo Citrato, Ã estudado o efeito da urÃia adicionada durante o passo de gelificaÃÃo de uma soluÃÃo contendo TiCl4, Pb(NO3)2, ZrOCl2.8H2O e Ãcido cÃtrico como agente quelante. A quantidade de ur
Publicado em: 2002