Porous Titanium
Mostrando 1-12 de 34 artigos, teses e dissertações.
-
1. Oxidation Behavior of Al-Y Coating on γ-TiAl at 900°C
ABSTRACT In this study, an Al-Y coating was applied to enhance the property of oxidation resistance on the surface of γ-TiAl alloys by rf magnetron sputtering. The isothermal oxidation tests were investigated at 900 °C for 100 h. The coating characteristics and microstructure of coating after isothermal oxidation were inspected by XRD and SEM methods respe
Matéria (Rio J.). Publicado em: 20/05/2019
-
2. Estructuras de titanio con gradiente de porosidad – fabricación por el método de partículas espaciadoras y caracterización
ABSTRACT It has proposed the use of porous titanium to reduce the problem of mechanical incompatibility, which occurs between such material used in implants and bone. The pores introduction in titanium decreases its elastic modulus by bringing it closer to that of both cortical and trabecular bones. This paper describes titanium fabrication by powder metallu
Matéria (Rio J.). Publicado em: 19/07/2018
-
3. Obtención de compuesto de titanio con gradiente de porosidad mediante técnica pulvimetalúrgica
ABSTRACT Within the study of biomaterials for implantological use titanium is among the most widely employed metals due to its excellent corrosion and mechanical resistance. In spite of the advances made, there are some issues remaining with the value of the elastic moduli of the titanium (110GPa) in comparison with the elastic moduli of the cortical bone (2
Matéria (Rio J.). Publicado em: 19/07/2018
-
4. Recubrimientos porosos de dióxido de titanio sintetizados por oxidación anódica
ABSTRACT Titanium dioxide is one of the most used materials in heterogeneous photocatalysis due to its commercial availability, low cost, chemical stability, low toxicity and high photocatalytic activity. One of the most efficient and economical methods to obtain TiO2 coatings is the plasma electrolytic oxidation. In this anodization process, a direct curren
Matéria (Rio J.). Publicado em: 19/07/2018
-
5. Caracterización de compositos biocerámicos en esponjas de titanio mediante interpenetración por corriente pulsada asistida
ABSTRACT Recently, it has been directing some special attention to the development of new manufacturing processes, with engineering applications in human tissues [1]. 3D printing applied to tissue engineering requires pulse computational techniques such as stereolithographic modeling, and special manufacturing processes, to name a few; Laser Sintering or Ext
Matéria (Rio J.). Publicado em: 19/07/2018
-
6. In Situ Formation of Hydroxyapatite During Powder Metallurgy Preparation of Porous Ti/HA Nano Composite: A Candidate for Dental Implants
Porous Ti/HA nano-composite was prepared for implant fixtures and in situ formation of Hydroxyapatite. At first, Ca(OH)2 nanoparticles were synthesized by precipitation. Raw materials included Ca(NO3)2.4H2O, NaOH, a mixture of deionized water and ethanol. Synthesized Ca(OH)2 nano powder was mixed with (NH4)2HPO4 and the mixture was calcined at 700 ºC for 30
Mat. Res.. Publicado em: 28/05/2018
-
7. Porous Titanium Associated with CaP Coating: In Vivo and In Vitro Osteogenic Performance
This in vitro and in vivo study compared different topographies of Ti samples (dense, porosity of 30% and 40%) with or not CaP coating, prepared by powder metallurgy. Osteogenic cells from newborn rat calvaria were plated onto the samples and cell adhesion (24 hours), alkaline phosphatase activity (7 and 10 days) and mineralization nodules (14 days) were ass
Mat. Res.. Publicado em: 18/12/2017
-
8. A Novel Porous Diamond - Titanium Biomaterial: Structure, Microstructure, Physico-Mechanical Properties and Biocompatibility
ABSTRACT With the aim of introducing permanent prostheses with main properties equivalent to cortical human bone, Ti-diamond composites were processed through powder metallurgy. Grade 1 titanium and mixtures of Ti powder with 2%, 5% and 10 wt% diamond were compacted at 100MPa, and then sintered at 1250°C/2hr/10-6mbar. Sintered samples were studied in the po
An. Acad. Bras. Ciênc.. Publicado em: 11/12/2017
-
9. Osseointegration aspects of placed implant in bone reconstruction with newly developed block-type interconnected porous calcium hydroxyapatite
ABSTRACT Artificial bone has been employed to reconstruct bone defects. However, only few reports on implant placement after block bone grafting exist. Objectives The purpose of this study was to evaluate the osseointegration of dental implant in bone reconstructions with interconnected porous calcium hydroxyapatite (IP-CHA). Material and Methods The IP-
J. Appl. Oral Sci.. Publicado em: 2016-08
-
10. Estudo in vitro e in vivo da osseointegração de implantes de titânio com superfícies biomimetizadas / In Vitro and in vivo study of the osseointegration of titanium with biomimetics surfaces
As pesquisas realizadas com implantes procuram melhorar a qualidade dos produtos com o objetivo de reduzir o tempo de espera após a cirurgia para submeter os implantes às cargas mastigatórias com segurança. Para atender esta expectativa deve-se considerar que o organismo tem um tempo mínimo para realizar as reações que levam à osseointegração. O pr
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 30/03/2012
-
11. Modification of the titanium oxide morphology and composition by a combined chemical-electrochemical treatment on cp Ti
A combined chemical-electrochemical oxidation method to obtain porous bioactive TiO2 films on titanium is reported. In this case, a titanium chemical pre-etching followed by the micro-arc oxidation (MAO) treatment is proposed and optimized, to obtain a high-roughness and porous surface which benefits the titanium/bone integration. The MAO treatment at variou
Materials Research. Publicado em: 20/01/2012
-
12. Enhanced photocatalytic activity of TiO2 films by modification with polyethylene glycol
Titanium dioxide porous thin films on the Anatase phase were deposited onto glass slides by the sol-gel method assisted with polyethylene glycol (PEG). The dip-coated films were characterized using scanning electron microscopy (SEM), thermogravimetric analysis (TGA and DTG), UV-visible spectroscopy and X-ray diffraction (XRD). The photocatalytic activity of
Quím. Nova. Publicado em: 2012