Pin On Disc Test
Mostrando 1-10 de 10 artigos, teses e dissertações.
-
1. Tribology of natural Poly-Ether-Ether-Ketone (PEEK) under transmission oil lubrication
Abstract High performance polymeric materials such as poly-ether-ether-ketone (PEEK) are increasingly being used for challenging tribological applications in order to replace metal parts in vehicle engines and transmissions. The tribology of natural PEEK, under oil-lubricated conditions, was studied for different metal counterbody finishes. Two different fin
Polímeros. Publicado em: 04/07/2019
-
2. Study of Mechanical and Wear Behaviour of Hyper-Eutectic Al-Si Automotive Alloy Through Fe, Ni and Cr Addition
Effect of Fe, Ni and Cr addition on the wear behavior of hyper-eutectic Al-Si automotive alloy has been studied. Dry sliding wear tests have been conducted using pin-on-disc wear testing machine under normal loads of 20N and constant sliding speed of 0.64 ms-1. Influence of Fe addition to the base alloy increases the wear rate due to the formation of needle
Mat. Res.. Publicado em: 11/06/2018
-
3. The correlation between tribological properties of nanostructure TiN coatings and deposition process parameters in PACVD system
ABSTRACT Titanium base coatings are being used extensively for improving wear characteristics at the surface of different parts. Titanium nitride was deposited by Plasma Assisted Chemical Vapor Deposition (PACVD) techniques with purpose improve interface with substrate, as this can increase wearing of the entire part in spite of desirable wear behavior of Ti
Matéria (Rio J.). Publicado em: 22/06/2017
-
4. Influence of Tungsten on Dry Sliding Wear Behaviour of Sintered/Hot Extruded P/M Alloy Steels (Fe-C-W-Ti)
In the present scenario, Powder Metallurgy (P/M) is an established manufacturing process used to make components of complex geometries with high strength and tolerances by using incredible materials which are difficult to melt or form by other processes. The mechanical properties and microstructures will determine the component characteristic dependent on th
Mat. Res.. Publicado em: 08/06/2017
-
5. Deposition of Multicomponent Chromium Carbide Coatings Using a Non-Conventional Source of Chromium and Silicon with Micro-Additions of Boron
The chromium carbide coatings are widely used in the mechanical industry due to its corrosion resistance and mechanical properties. In this work, we evaluated a new source of chromium and silicon with micro-additions of boron on the deposition of multi-component coatings of chromium carbides in W108 steel. The coatings were obtained by the pack cementation m
Mat. Res.. Publicado em: 05/01/2017
-
6. Effect of surface finishing on friction and wear of Poly-Ether-Ether-Ketone (PEEK) under oil lubrication
Abstract The tribological properties of poly-ether-ether-ketone (PEEK) containing 30% of carbon fiber were studied in an oil-lubricated environment and different surface finishing of the metallic counterbody. Four different finishing processes, commonly used in the automotive industry, were chosen for this study: turning, grinding, honing and polishing. The
Polímeros. Publicado em: 08/12/2016
-
7. Investigation on the Wear Behaviour of Eutectic Al-Si Alloy- Al2O3 - Graphite Composites Fabricated Through Squeeze Casting
Dry sliding wear test was conducted on Al -Si alloy - Al2O3 - Graphite composites which are fabricated through squeeze casting method, using pin -on -disc wear testing rig. The influence of parameters such as applied load, sliding velocity and weight percentage of graphite, on the wear loss of Al- 5 wt. % Al2O3 - Graphite hybrid composite was investigated th
Mat. Res.. Publicado em: 27/06/2014
-
8. Estudo do comportamento tribológico do aço AISI H13 submetido a tratamento termoquímico de boretação / Study of tribological behavior of AISI H13 steel subjected to boriding thermochemical treatment
In this work, solid boriding thermochemical treatment was carried out using Ekabor 1-V2 and one blend as boriding agents and heat treatment of quenching and tempering of AISI H13 tool steel in order to compare and evaluate the tribological behavior and the properties acquired for four studied conditions, that were: Ekabor powder boriding, Ekabor powder borid
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 18/06/2012
-
9. Estudo do desgaste abrasivo e adesivo em aços ferramenta por meio do ensaio de pino-disco / Study of abrasive and adhesive wear in tool steels by pin-on-disc test
Entre os diversos mecanismos de desgaste, os desgastes abrasivo e adesivo são os que respondem pela maior contribuição nas falhas em equipamentos e ferramentais da indústria mecânica. Ferramentas utilizadas na fabricação de estatores, conhecidas como lamelas, falham em decorrência destes tipos de desgaste. As falhas têm procedência no desgaste por
Publicado em: 2011
-
10. Caracterização do comportamento de desgaste de cerâmicas de alumina densa : efeitos de parâmetros do ensaio do tipo pino no disco / Characterization of the wear behavior of dense alumina ceramics: effects of the pin-on-disc test parameters
Na busca por materiais resistente ao desgaste, atenção tem sido dada a cerâmicas como Si3N4, SiC, Al2O3 e ZrO2, por apresentarem melhores características quando comparadas com outros materiais. Apesar da fragilidade destas cerâmicas, pelo melhoramento no processamento e pela introdução de segundas fases nas matrizes cerâmicas, algumas propriedades me
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 08/12/2010