13. Intercritical Heat Treatment Temperature Dependence of Mechanical Properties and Corrosion Resistance of Dual Phase Steel
Abstract This study investigated the effect of intercritical heat treatment temperature on the tensile properties, work hardening and corrosion resistance of dual phase steel. Ferrite-martensite dual phase steel with different martensite volume fractions were obtained after heat treatment at different intercritical temperatures. Microstructure, mechanical pr
Mat. Res.. Publicado em: 17/01/2019
-
14. Effect of Aging Heat Treatment H950 and H1000 on Mechanical and Pitting Corrosion Properties of UNS S46500 Stainless Steel
The effect of aging temperature on mechanical and pitting corrosion properties of UNS S46500 was investigated. Tensile and Hardness tests were carried out and the microstructure was analyzed by optical microscopy, scanning electron microscopy and X-ray diffraction; Thermo-Calc simulations helped in the phase identification. Pitting corrosion properties were
Mat. Res.. Publicado em: 08/11/2018
-
15. The Influence of Microstructure and Mechanical Resistance on the Shape Memory of Ecae Processed Stainless Fe-Mn-Si-Cr-Ni-Co Steel
In the current work, XRD, SEM, EBSD and TEM techniques were used to evaluate the microstructure of stainless Fe-Mn-Si-Cr-Ni-Co shape memory steel processed by ECAE and annealed for one hour at temperatures ranging from 650ºC to 950ºC. The results were then correlated with the mechanical and shape-memory properties of the steel. It was observed that the sam
Mat. Res.. Publicado em: 09/08/2018
-
16. 3D Microstructural Finite Element Simulation of Martensitic Transformation of TRIP Steels
Abstract In this paper the effects of deformation modes on martensitic transformation for TRIP steels which are composed of Ferrite, Bainite and Retained austenite are investigated in the view of the microstructural level. For this porpose the simulations are run for a synthetically generated microstructure which have 55% Ferrit, 35% Bainite and 10% Retained
Lat. Am. j. solids struct.. Publicado em: 30/07/2018
-
17. Characterization of Phase Transformations and Microstructural Changes in an API 5CT L80 Steel Grade During Ni Alloy Laser Cladding
The superficial coatings in micro-alloyed steel pipes has been a pointed way to decrease the corrosion problems in oil and gas industry. However, little emphasis has been given to the substrate. The effects of the deposition method on the steel microstructure and properties are still not well described. In this context, this work studied the effect of Ni sup
Mat. Res.. Publicado em: 26/07/2018
-
18. Characterization of reverse martensitic transformation in cold-rolled austenitic 316 stainless steel
ABSTRACT In this work the reversion of the strain-induced ?’-martensite to ?’-austenite was studied in a series of AISI 316 stainless steels (SS) specimens. The samples were submitted to 63% reduction in thickness by rolling at a temperature of -70ºC, to achieve high martensite content. The reversion of martensite to austenite was made by means of isoch
Matéria (Rio J.). Publicado em: 19/07/2018
-
19. Efecto del tratamiento sub-cero sobre la microestructura y dureza de fundiciones blancas alto cromo
ABSTRACT The effect of the sub-zero treatment temperature on the transformation of retained austenite to martensite in two high chromium white cast irons (ASTM A532 Class II Type B) was studied. The sub-zero treatment applied to each alloy in the as cast condition was performed at -40, -65 and -180 ° C for 10 minutes; after the holding time was completed th
Matéria (Rio J.). Publicado em: 19/07/2018
-
20. Determinación de los parámetros de austenización intercrítica para el desarrollo de aceros multifásicos mediante análisis dilatométrico
ABSTRACT The Multiphase steels are materials with exceptional mechanical properties including high strength, excellent ductility and hardening coefficient and good conformability. These properties are related with the microstructure, which can be a combination of ferrite and martensite (Dual phase steels) or more complex microstructures with ferrite, bainite
Matéria (Rio J.). Publicado em: 19/07/2018
-
21. Influence of defects on the irreversible phase transition in the Fe-Pd doped with Co and Mn
ABSTRACT The appearance of BCT martensite in Fe-Pd-based ferromagnetic shape memory alloys, which develops at lower temperatures than the thermoelastic martensitic transition, deteriorates the shape memory properties. In a previous work performed in Fe70Pd30, it was shown that a reduction in defects density reduces the non thermoelastic FCT-BCT transformatio
Matéria (Rio J.). Publicado em: 19/07/2018
-
22. Estabilidad de la austenita retenida bajo condiciones de deformación en aceros multifásicos con bainita nanoestructurada
ABSTRACT A steel with nominal composition 0.25C, 1.9Si, 0.63Mn, 1.5Cr was manufactured using an induction furnace. The as-cast alloy was homogenized and the temperatures of austenite start (AC1) and finish (AC3) during heating were determined by dilatometric analyses. Two intercritical austenitization temperatures were selected, which were used to perform pa
Matéria (Rio J.). Publicado em: 19/07/2018
-
23. Evolución microestructural in-situ a alta temperatura de depósitos de soldadura de aceros 9Cr con diferentes contenidos de boro
ABSTRACT New alloys have been developed for enhancing the performance of the equipment used in thermoelectric power generation industry. With the objective of increasing the creep resistance of these materials, changes in the content of some microalloying elements were carried out. Boron bearing in creep strength enhanced 9Cr steel (CSE9Cr) welds improved ma
Matéria (Rio J.). Publicado em: 19/07/2018
-
24. Obtención de aceros de baja aleación con diferentes contenidos de Ni y similares microestructuras y propiedades mecánicas
ABSTRACT Low alloy steels are used in many applications in the oil and gas industry. The addition of Ni in these steels improves their low temperature fracture toughness and hardenability, with a low penalty on weldability. However, ISO 15156-2 standard restricts Ni content up to a 1 wt% limit, requiring additional and expensive tests if higher Ni steels are
Matéria (Rio J.). Publicado em: 19/07/2018