Ligas De Naquel
Mostrando 1-11 de 11 artigos, teses e dissertações.
-
1. âRevestimento por soldagem MIG/MAG empregando ligas de nÃquel para apliacaÃÃes em componentes do setor de petrÃleo e gÃs naturalâ / Gmaw Welding Overlay Of Nickel-Based Alloys For Applications In Oil And Natural Gas Components
The weld overlay of nickel-based alloys is an alternative often used in oil and gas industry to prevent corrosion in pipes and equipments operating under severe conditions. In many situations the requirements of weld overlays are based in a maximum of 5% iron content in the weld metal to ensure corrosion resistance. The aim of this study was to determine the
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 03/12/2010
-
2. Revestimentos de liga de nÃquel depositados pelo processo TIG com alimentaÃÃo de arame frio: aspectos operacionais e metalÃrgicos / Nickel based alloys weld overlay deposited by gtaw cold wire feed: operational and metallurgical aspects
The weld overlay with nickel-based alloys is an interesting alternative for the construction and repair of equipments for applications in severe corrosive medium, allowing reach the desirable characteristics (corrosion resistance) with a significant reduction of cost. In this context, the GTAW cold wire feed process can be a good option for overlay depositio
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 09/04/2010
-
3. Revestimento de ligas de nÃquel pelo processo MIG/MAG com transferÃncia por curto-circuito / weld overlay with nickel alloy through the GMAW process in a short circuiting transfer mode.
Este trabalho teve como objetivo determinar os parÃmetros de soldagem que proporcionem condiÃÃes adequadas para revestimentos com ligas de nÃquel atravÃs do processo MIG/MAG com transferÃncia metÃlica por curto-circuito indicadas para aplicaÃÃes no setor de petrÃleo e gÃs natural. A primeira etapa consistiu na realizaÃÃo de ensaios exploratÃrio
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 19/10/2009
-
4. Estudo da atividade eletrocatalÃtica da reaÃÃo de desprendimento de hidrogÃnio (RDH) sobre cÃtodos de nÃquel e nÃquel-molibdÃnio / Study of the eletrocatalÃtica activity of the reaction of hydrogen unfastening (RDH) on cathodes of nickel and nickel-molybdenum
Nesse trabalho foram realizados estudos sobre a reaÃÃo de desprendimento de hidrogÃnio (RDH) em meio alcalino sob ligas de Ni-Mo obtidas por eletrodeposiÃÃo em diferentes condiÃÃes operacionais. Para efeito de comparaÃÃo tambÃm foram feitos testes em superfÃcies de Ni eletrodepositadas dentro das mesmas condiÃÃes utilizadas para as ligas de Ni-M
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 25/06/2009
-
5. Estudo exploratÃrio de parÃmetros de soldagem de revestimentos com ligas de NÃquel empregando o processo TIG com alimentaÃÃo de arame frio / Exploratory study of coating welding parameters with nickel alloys using GTAW with cold wire feeding
The aim of this work was to carry out a systematic study of GTAW welding parameters with feeding of cold wire for covering application of nickel alloys (UNS N06625, UNS N06686 and UNS N10276) in substract of steel C-Mn considering the analysis of geometric, economic and operational characteristics of layers, form to adjust these coverings for the industries
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 14/01/2009
-
6. AVALIAÃÃO DO REVESTIMENTO A BASE DE LIGA DE NÃQUEL EM AÃO ESTRUTURAL, EMPREGANDO O METAL DE ADIÃÃO ERNiCrMo-3 ATRAVÃS DA SOLDAGEM MIG/MAG / EVALUATE OF NICKEL WELD OVERLAY IN STRUCTURAL STEEL, WITH EMPLOYMENT OF GMAW ERNiCrMo-3 ELECTRODE.
The use of nickel alloy cladding components could be more frequently in petroleum industry. The crescent naphthenic corrosion and high molecular weight of national petroleum contribute for needs of materials with more resistance to corrosion, to temperature and to pressure. At this way, how part of systematic study, this work pretends to define operational r
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 04/04/2008
-
7. ProduÃÃo da liga Ni-Ti com efeito de memÃria de forma em forno de fusÃo por feixe eletrÃnico e sua caracterizaÃÃo.
A primeira etapa deste trabalho consiste de uma descriÃÃo geral das propriedades mecÃnicas, temperaturas de transformaÃÃo e caracterÃsticas microestruturais de uma liga Ni-50,2Ti(%at.) com Efeito de MemÃria de Forma (EMF) previamente produzida via fusÃo por feixe de elÃtrons (EBM). O comportamento mecÃnico foi estudado por ensaios de traÃÃo em co
Publicado em: 2007
-
8. AvaliaÃÃo do estiramento de chapas da liga AA 2024, para trÃs condiÃÃes distintas de tÃmpera.
O processo de estiramento consiste na conformaÃÃo de chapas, barras e seÃÃes laminadas ou extrudadas, pelo "esticamento" do material sobre uma ferramenta (bloco) que contÃm a forma (linha de sistema) desejada. Este processo à utilizado principalmente na fabricaÃÃo de peÃas da indÃstria aeroespacial. Os materiais empregados sÃo ligas de alumÃnio,
Publicado em: 2007
-
9. EletrodeposiÃÃo de CuNi em meio de sulfato. uma nova abordagem / electroplating of cuni in sulphate.a new boarding
O interesse pela eletrodeposiÃÃo de CuNi e suas mÃltiplas camadas à principalmente devido Ãs propriedades destes materiais, tais como: resistÃncia à corrosÃo, propriedades mecÃnicas (alta forÃa de traÃÃo, maleabilidade e ductilidade) e magnÃticas, alÃm de suas propriedades catalÃticas. Os resultados voltamÃtricos deste trabalho sugerem que a
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 04/09/2006
-
10. ESTUDO COMPARATIVO ENTRE CINCO LIGAS DE NÃQUEL-CROMO NO TOCANTE A FLUIDEZ E CONSEQÃENTE REPRODUTIBILIDADE / Comparative study of five Ni-Cr alloys concerning castability and reproducibility.
The aim of this study was to verify the behavior of five brands of NiCr alloys, indicated to porcelain fused to metal restorations, comparing the castability with the ability of reproducing the thin edges of restoration margins. The samples were divided in five groups, each one for one brand, with ten repetitions for castability test and ten for edge reprodu
Publicado em: 2004
-
11. Estudo de um mecanismo de retenÃÃo/liberaÃÃo utilizando liga com efeito de memÃria de forma.
Este trabalho descreve um estudo detalhado de um mecanismo de retenÃÃo/liberaÃÃo de apÃndices de satÃlites baseado em liga com efeito de memÃria de forma como alternativa para mecanismos pirotÃcnicos e de cera derretida. Foi utilizado como base para os requisitos de projeto do dispositivo, a configuraÃÃo do satÃlite SACI II, projetado e fabricado
Publicado em: 2000