1. Effects of Heat Treatment and Yb 3+ Concentration on the Downconversion Emission of Er 3+ /Yb 3+ Co-Doped Transparent Silicate Glass-Ceramics
The SiO2-Al2O3-BaF2-TiO2-CaF2 transparent silicate glass-ceramics containing BaF2 nanocrystals were successfully prepared by heat treatment process through conventional melting method. Effects of heat treatment processes and Yb3+ concentration on the downconversion (DC) emission of the co-doped Er3+/Yb3+ transparent silicate glass-ceramics were investigated.
Mat. Res.. Publicado em: 28/10/2019
-
2. Reinforced Glass-ceramics: Parametric Inspection of Three-Dimensional Wear and Volumetric Loss after Chewing Simulation
Resumo O objetivo deste estudo foi investigar o desgaste tridimensional, perda volumétrica e rugosidade após a simulação de mastigação de dois materiais vitro-cerâmicos. Discos de dissilicato de lítio (LD, Emax CAD, Ivoclar) e silicato de lítio reforçado com zircônia (ZLS, Vita Suprinity, Vita Zhanfabrick) (n=20/g) foram confeccionados e digitaliz
Braz. Dent. J.. Publicado em: 07/10/2019
-
3. Characterization of Li2O-Al2O3-SiO2 glass-ceramics produced from a Brazilian spodumene concentrate
Resumo Vitrocerâmicas do sistema LAS (Li2O-Al2O3-SiO2) com elevada resistência ao choque térmico foram obtidas com sucesso com o uso de um concentrado de espodumênio brasileiro como principal matéria-prima (80%-70% em massa). Duas composições (Li2O.Al2O3.nSiO2) foram produzidas com n= 2 e 4, próximas às composições estequiométricas das fases eucr
Cerâmica. Publicado em: 15/08/2019
-
4. Dental ceramics: a review of new materials and processing methods
Abstract The evolution of computerized systems for the production of dental restorations associated to the development of novel microstructures for ceramic materials has caused an important change in the clinical workflow for dentists and technicians, as well as in the treatment options offered to patients. New microstructures have also been developed by the
Braz. oral res.. Publicado em: 28/08/2017
-
5. Crystallization of Anatase TiO2 in Niobium Potassium Phosphate Glasses
In this work, the glass forming ability was studied in potassium phosphate glasses with increasing amounts of TiO2 in order to obtain a glass-ceramic with photocatalytic properties. The first studied series has been the binary system (100-x) KPO3-xTiO2. Homogeneous and transparent glasses could be obtained with x varying from 10 to 30 mole%. Since the photoc
Mat. Res.. Publicado em: 16/02/2017
-
6. Influence of the interposition of ceramic spacers on the degree of conversion and the hardness of resin cements
This study evaluated: I) the effect of photo-activation through ceramics on the degree of conversion (DC) and on the Knoop hardness (KHN) of light- and dual-cured resin cements; and II) two different protocols for obtaining the spectra of uncured materials, to determine the DC of a dual-cured resin cement. Thin films of cements were photo-activated through c
Braz. oral res.. Publicado em: 2013-09
-
7. Influência dos precursores de prata no crescimento de nanopartículas metálicas em vidros óxidos de metais pesados
In this work we report a systematic study on the influence of the chemical nature of silver precursors on the formation of glass-ceramics from oxide glasses. Thermal, structural and optical properties were analyzed as a function of the glass composition. Controlled crystallization was achieved by thermal treatment of the samples above glass transition. The i
Quím. Nova. Publicado em: 2013
-
8. Expressão das proteínas citoesqueléticas actina e tubulina em células osteogênicas cultivadas sobre vidro e vitrocerâmica bioativos / Expression of the cytoskeletal proteins actin and tubulin in osteogenic cells cultured on bioactive glass-based surfaces
Bioactive glasses and glass-ceramics have been successfully applied in various therapeutic strategies to promote the formation of mineralized matrix in bone defects. The exposure of these materials to biological fluids results in chemical and topographical modifications that may affect the interactions of cells with the biomaterial surface, with potential ef
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 03/08/2012
-
9. Crescimento super e subcrítico de trincas em vidros e vitrocerâmicos analisado via indentação / Super and Subcrtical Crack Growth in Bioglasses and Glass-ceramics Analized Via Indentation
Nesta dissertação quantificamos propriedades que possam descrever melhor o comportamento mecânico de diferentes vidros e vitrocerâmicos do sistema Na2O-CaO-SiO2-P2O5 após a implantação no corpo humano, baseados na composição do Biosilicato anteriormente desenvolvido no LaMaV-UFSCar. Tentamos analisar variáveis como o n (parâmetro de susceptibilida
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 02/07/2012
-
10. Avaliação de cimentos de ionômero de vidro modificados por resina frente à incorporação de nanopartículas de vitrocerâmica bioativa / Resin modified glass ionomer cements evaluation with additional bioactive glass-ceramics nanoparticles
Os materiais bioativos são materiais sintéticos que possuem superfícies ativas em que os minerais presentes em tecidos duros podem se ligar quimicamente. Há alguns estudos em Odontologia, onde partículas desses materiais foram incorporadas aos Cimentos de Ionômero de Vidro (CIVs) e Cimentos de Ionômero de Vidro modificados por resina (CIVMRs) com o ob
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 31/05/2011
-
11. Biovidros e vitrocerâmicos bioativos do sistema 3Ca0.P205-Si02-MgO para aplicações biomédicas: processamento e caracterizações estruturais mecânicas e biológicas / Biglasses and bioactive glass-ceramics based on 3CaO.P2O5-SiO2-MgO-system for biomedical applications: processing, and structural, mechanical and biological characterization
Este trabalho apresenta o desenvolvimento e a caracterização de biovidros e vitrocerâmicos bioativos do sistema 3CaO.P2O5-SiO2-MgO, com índices de cristalinidade variados, visando o uso destes materiais em implantes estruturais ósseos. Amostras de composição nominal (% em peso) 57,75% CaO.P2O5 - 30% SiO2 - 17,25% MgO foram obtidas por fusão, e poster
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 27/01/2011
-
12. Biosilicato®: histórico de uma vitrocerâmica brasileira de elevada bioatividade
This paper presents a historical of the Biosilicate®, a bioactive glass-ceramic developed at the Vitreous Materials Laboratory of the Federal University of São Carlos, Brazil. After decades of study accomplished with bioactive glasses and glass-ceramics, Biosilicate® results from a natural evolution and has similar bioactivity index, but far superior mech
Química Nova. Publicado em: 2011