Fosfato Tricalcio 946
Mostrando 1-4 de 4 artigos, teses e dissertações.
-
1. Síntese e caracterização de pós de fosfato tricálcio-β e de hidroxiapatita: elaboração de bifásicos HA/TCP-β para aplicações como substituto ósseo / Synthesis and characterization of powders of β -Tricalcium phosphate and hydroxyapatite: elaboration of HA/β -TCP biphasic for applications as bone substitute
The treatments of bone loss are current topics of research. The materials that stand out in the treatments of reconstruction and formation of new bone tissue, are the hydroxyapatite, the α and/or β calcium phosphates, and biphasic hydroxyapatite / α and/or β calcium phosphate. It is known from literature that these biomaterials h
Publicado em: 2011
-
2. Processamento de hidroxiapatita por microondas: sÃntese de pÃs e sinterizaÃÃo de peÃas / Processing of hydroxyapatite by microwave irradiation: synthesis of powder and sintering of parts
As biocerÃmicas sÃo substÃncias ou combinaÃÃo de substÃncias que tem aplicabilidade clÃnica, com a finalidade de restituir ou tratar ÃrgÃos, tecidos ou funÃÃes do corpo humano. SÃo quimicamente muito estÃveis e, portanto, pouco provÃveis de induzir uma resposta biolÃgica adversa. As biocerÃmicas mais empregadas na reconstituiÃÃo de tecidos
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 22/12/2009
-
3. Obtenção de cerâmicas à base de tricálcio fosfatos utilizando óxido de magnésio como aditivo
The tricalcium phosphate ceramics has been widely investigated in the last years due its bioresorbable behavior. The limiting factor of the application of these materials as temporary implants is its low strength resistance. The tricalcium phosphate presents an allotropic transformation β→α around 1250 C that degrades its resistance. Some stu
Publicado em: 2007
-
4. Obtenção de cerâmicas à base de tricálcio fosfatos utilizando óxido de manganês como aditivo
The calcium phosphate ceramics have been very investigated as material for bone implants. The tricalcium phosphate (β-TCP) had a great potential for application in temporary implants like a resorbable bioceramic. This material presents a limitation in its sintering temperature due to occurrence of the allotropic transformation β → α at
Publicado em: 2006