1. Morphology Behavior of Copper Films Deposited after Wet Surface Treatment on Polished Alumina
In this paper, a pre-treatment process for electroless copper (Cu) deposition on the polished alumina (Al2O3) 99.9% and the behavior of Cu plating by electroless process after Al2O3 surface treatment were explored. Our work was carried out by changing the roughness of Al2O3 through micro-etching (coarsening), nucleation its surface by a two-step method (sens
Journal of the Brazilian Chemical Society. Publicado em: 2022
-
2. Characterization of copper microelectrodes, following a homemade lithography, technique, and gold electroless deposition
We report the fabrication and characterization of copper microelectrodes obtained by a homemade lithography technique and after gold electroless deposition. For the fabrication, planes consisting of arrays of electrodes (black in color) with bow tie shape were designed and printed on a transparent paper (Canson ltd.). Using an embroidery frame with a silk fa
Matéria (Rio J.). Publicado em: 2016-03
-
3. Fabricação e caracterização de termopares Cu/CuNixPy obtidos por deposição eletroquímica. / Fabrication and characterization of Cu/CuNixPy thermocouples obtained by electroless deposition.
In this work, it was studied chemical depositions of CuNixPy alloys and it was fabricated Cu/CuNixPy thermocouples onto silicon wafer surfaces. Initially, surfaces were pre-activated in a diluted hydrofluoric acid solution containing PdCl2. Following, it was used a de-ionizedwater- diluted alkaline chemical bath containing 15 g/l NiSO4.6H2O; 0,1-0,3 g/l CuSO
Publicado em: 2008
-
4. Avaliação da replicagem de moldes torneados com ferramenta de diamante usando prensagem a quente em polimetilmetacrilato (PMMA) / Evaluation of the replication of molds generated from single point diamond turning using hot embossing in polymethylmethacrylate (PMMA)
In this work, different types of microstructures were generated by single point diamond turning and microindentation for will replicated through the hot embossing. Tests were carried to evaluate the generation these microstructures by two distinct methods: micro-deformation and micro-machining, planned to observe the replication of the mark generated by the
Publicado em: 2006