1. Effect of software version and parameter settings on the marginal and internal adaptation of crowns fabricated with the CAD/CAM system
Objective This study investigated the marginal and internal adaptation of individual dental crowns fabricated using a CAD/CAM system (Sirona’s BlueCam), also evaluating the effect of the software version used, and the specific parameter settings in the adaptation of crowns. Material and Methods Forty digital impressions of a master model previously pre
J. Appl. Oral Sci.. Publicado em: 2015-10
-
2. Evaluation of the adaptation of zirconia-based fixed partial dentures using micro-CT technology
The objective of the study was to measure the marginal and internal fit of zirconia-based all-ceramic three-unit fixed partial dentures (FPDs) (Y-TZP - LAVA, 3M-ESPE), using a novel methodology based on micro-computed tomography (micro-CT) technology. Stainless steel models of prepared abutments were fabricated to design FPDs. Ten frameworks were produced wi
Braz. oral res.. Publicado em: 2013-09
-
3. Microleakage in combined amalgam/composite resin restorations in MOD cavities
AIM: To compare marginal seal at tooth-material and material-material interfaces in the proximal box in combined amalgam/composite resin restorations. METHODS: Mesio-occlusal-distal (MOD) cavities were prepared in 35 premolars and permanent molars with carbide bur. The distal proximal box was restored with amalgam (Permite, SDI) until reaching the height of
Braz. J. Oral Sci.. Publicado em: 2013-06
-
4. Stress distribution and screw detorque analysis : influence of misfit and alloy types in cast implant retained frameworks / Avaliação das tensões e do destorque de parafusos : influência do desajuste marginal e dos tipos de metais em infraestruturas protéticas retidas por implantes
O objetivo neste estudo foi avaliar a distribuição das tensões geradas aos implantes modificados, por meio de análise extensométrica e força de destorque dos parafusos de retenção protética, de acordo com o tipo de metal da infraestrutura (Titânio comercialmente puro - Ti c.p ou Cobalto-Cromo - Co-Cr) e presença ou ausência de desajuste vertical
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 10/02/2012
-
5. A new portable vibrator for plaster pouring: effect on the marginal fit at cylinder-abutment
OBJECTIVE: The aim of this study was to test a new portable vibrator for plaster pouring (developed for this purpose), comparing the effect of its use on the accuracy of working cast of implant-supported restorations to the conventional vibrator. MATERIAL AND METHODS: From a master cast with 2 implants, 30 transfer moldings were made randomly and divided int
J. Appl. Oral Sci.. Publicado em: 2012-10
-
6. Influência da espessura da resina de baixa viscosidade e da técnica restauradora na infiltração marginal em restaurações realizadas com compósito dental / Influence of the thickness of two flowable composite resins and the restorative technique on microleakage of simulated class II composite resin restorations
O objetivo deste estudo in vitro foi avaliar quantitativamente a infiltração marginal ao redor de restaurações dentais, realizadas com compósito resinoso microhíbrido, variando a espessura, a resina de baixa viscosidade e a técnica restauradora. As superfícies proximais de cento e trinta incisivos bovinos foram preparadas e divididas de acordo com a
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 10/06/2011
-
7. Effects of resin luting agents and 1% NaOCl on the marginal fit of indirect composite restorations in primary teeth
OBJECTIVE: The purpose of this study was to provide information regarding the marginal adaptation of composite resin onlays in primary teeth previously treated with 1% sodium hypochlorite (NaOCl) (pulp irrigant) using two different resin luting agents. MATERIAL AND METHODS: Forty extracted sound primary molars had their crowns prepared in a standardized mach
Journal of Applied Oral Science. Publicado em: 2011-10
-
8. Comparative study of the adaptation between metallic copings, In-Cream alumina and e.max Press, before and after cementation / Estudo comparativo da adaptação marginal entre copings metalicos, In-Ceram alumina e e.max Press, antes e apos a cimentação
Esse estudo avaliou a adaptação marginal entre copings metálicos, In-Ceram e e.max Press, antes e após cimentação em preparos sobre dentes bovinos, utilizando dois tipos de cimento resinosos. Noventa incisivos bovinos foram fixados em resina acrílica ativada quimicamente e as porções coronárias foram preparadas para coroa total, com expulsividade d
Publicado em: 2010
-
9. Desajuste marginal e influencia na pre-carga de parafusos e nas tensões induzidas as fixações de pilares metaloplasticos sobre-fundidos / Marginal misfit and influence in the pre-load and the stress-induced setting of the metaloplastic abutments
Castable UCLA abutments are of wide applicability in dental implants, because they allow the manipulation in the laboratory at low cost and individualization of abutments for each patient. However, they show the worse results of marginal adaptation then the fabricated, although these aggregate costs significantly higher. UCLA premachined abutments for castin
Publicado em: 2010
-
10. Study and optimization of photocuring processes of composite resins to dental jobs. / Estudo e otimização da fotocura de resinas compostas de emprego odontológico
The aim of this study was to investigate the optimization of photo-cure of dental composite resin by combined curing methods. The curing was performed associating ultrasound and LED and LED with pre-heating composite resin. The irradiation performed was centered at 470 nm with power density of 600 mW/cm2 for the ultrasound and pre-heating association. The ap
Publicado em: 2010
-
11. Importance of three techniques of cavity preparation and three adhesive systems on microleakage of composite resin restorations / Importância de três técnicas de preparo cavitário e de três sistemas adesivos na microinfiltração marginal em restaurações Classe V de resina composta
This in vitro study compared the microleakage of class V resin composite restorations placed in cavities prepared with high-speed dental bur (AR), ultrasonic preparation devices (US) and high-speed dental bur plus ultrasonic preparation devices(AR+US), and restored using three different adhesive systems (One all etch Single Bond (SB) , and two Self-etch Clea
Publicado em: 2010
-
12. Evaluation of marginal adaptation, bond strength and nanoleakage of indirect restorations using resin coating technique and resin cement / Avaliação da adaptação marginal, resistencia de união e nanoinfiltração de restaurações indiretas utilizando a tecnica de selamento dentinario e cimento resinoso
As restaurações estéticas indiretas têm sido a opção de escolha no caso de cavidades extensas. No entanto, este tipo de restauração demanda um desenho de preparo muito mais invasivo, podendo levar a sensibilidade pós-operatória, assim como também, certa incompatibilidade entre o cimento resinoso e o adesivo. Na tentativa de solucionar estas limita
Publicado em: 2009