13. Chlorhexidine and proanthocyanidin enhance the long-term bond strength of resin-based endodontic sealer
Abstract The aim of this study was to evaluate the effects of proanthocyanidin (PA) and chlorhexidine (CHX) on the bond strength (BS), failure pattern, and resin-dentin interface morphology of the endodontic sealers EndoREZ and AH Plus after 24 h and 6 months of water storage. A total of 120 prepared bovine roots were divided into six groups: AH Plus, CHX+AH
Braz. oral res.. Publicado em: 24/05/2018
-
14. Push-out bond strength of different tricalcium silicate-based filling materials to root dentin
Abstract: The aim of this study was to evaluate the bond strength of different triccalcium silicate cements to retrograde cavity using a push out test. Thirty maxillary central incisors were shaped using #80 hand files and sectioned transversally. Root slices were obtained from the apical 4 mm after eliminating the apical extremity. The specimens were embedd
Braz. oral res.. Publicado em: 08/03/2018
-
15. Mode I Interlaminar Fracture Toughness Analysis of Co-Bonded and Secondary Bonded Carbon Fiber Reinforced Composites Joints
Aiming to reduce aircraft weight, aeronautic industry seeks alternative materials and processes used to join its different structural parts. An option to traditional methods are high performance adhesive joints, which reduce weight, number of parts and component final cost, also resulting in higher strength structures. Although, the lack of experimental data
Mat. Res.. Publicado em: 05/02/2018
-
16. Dentin pretreatment and adhesive temperature as affecting factors on bond strength of a universal adhesive system
Abstract Objectives: To evaluate the effects of dentin pretreatment and temperature on the bond strength of a universal adhesive system to dentin. Material and Methods: Ninety-six extracted non-carious human third molars were randomly divided into 12 groups (n=8) according to Scotchbond Universal Adhesive (SbU) applied in self-etch (SE) and etch-and-rinse
J. Appl. Oral Sci.. Publicado em: 2017-10
-
17. Bonded Joints with “Nano-Stitches”: Effect of Carbon Nanotubes on Load Capacity and Failure Modes
Abstract Carbon nanotubes were employed as adhesive reinforcement/nano-stitches to aluminum bonded joints. The CNT addition to an epoxy adhesive not only lead to an increase on load capacity but it is also the most probable cause of the mixed failure mode (adhesive/cohesive). The damage evolution was described as the stiffness decrease and the failure mixed
Lat. Am. j. solids struct.. Publicado em: 2017-03
-
18. Root filling bond strength using reciprocating file-matched single-cones with different sealers
Abstract The aim of the present study was to evaluate the bond strength (BS) of root canal fillings to root dentin using the reciprocating file-matched single-cone or lateral compaction techniques with resin-based and calcium-silicate-based sealers. Maxillary canine roots were prepared and filled using one of the following approaches: Reciproc R40 file and R
Braz. oral res.. Publicado em: 20/05/2016
-
19. Tensile Bond Strength of a Soft Liner to an Acrylic Resin after Primer Application and Thermocycling
Purpose: The aim of this study was to evaluate the effect of a surface treatment with Sofreliner primer on tensile bond strength of a resin-based soft liner (Coe-Soft) bonded to a polymethylmethacrylate (PMMA) resin before and after accelerated aging simulated by a thermocycling machine. Material and Methods: One hundred and twenty rectangular specimens of
Mat. Res.. Publicado em: 04/12/2015
-
20. Bonding durability of dental sealants to deciduous and permanent teeth
AIM: To evaluate the bonding durability of materials used as sealants on different dentitions. METHODS: Deciduous (D) and permanent (P) molars were divided into four groups (n=5) and sealed with Fluroshield (F) and OptiBond FL (FL). Blocks of composite resin were built, stored in distilled water (24 h/37 °C), sectioned into 0.8 mm2 and tested at tensi
Braz. J. Oral Sci.. Publicado em: 2014-09
-
21. Push-out bond strength of fiber posts to root dentin using glass ionomer and resin modified glass ionomer cements
OBJECTIVE: The purpose of this study was to assess the push-out bond strength of glass fiber posts to root dentin after cementation with glass ionomer (GICs) and resinmodified glass ionomer cements (RMGICs). MATERIAL AND METHODS: Fifty human maxillary canines were transversally sectioned at 15 mm from the apex. Canals were prepared with a step back techni
J. Appl. Oral Sci.. Publicado em: 04/07/2014
-
22. Micro-shear bond strength and surface micromorphology of a feldspathic ceramic treated with different cleaning methods after hydrofluoric acid etching
Objective: The aim of this study was to evaluate the effect of feldspathic ceramic surface cleaning on micro-shear bond strength and ceramic surface morphology. Material and Methods: Forty discs of feldspathic ceramic were prepared and etched with 10% hydrofluoric acid for 2 minutes. The discs were randomly distributed into five groups (n=8): C: no tre
J. Appl. Oral Sci.. Publicado em: 2014-04
-
23. Shear bond strength of a "solvent-free" adhesive versus contemporary adhesive systems
AIM: To compare the shear bond strength (SBS) of a solvent free self-etch adhesive with solvent containing adhesives. METHODS: Forty-five human teeth were sectioned longitudinally to expose superficial dentin and substrates polished with 600-grit SiC paper. The adhesive area was isolated with a cylindrical Teflon mold 3x4 mm. Fifteen specimens were pre
Braz. J. Oral Sci.. Publicado em: 2014-03
-
24. Effect of calcium hydroxide dressing on push-out bond strength of endodontic sealers to root canal dentin
The aim of the present study was to evaluate the effect of calcium hydroxide dressing on the bond strength of three commercially available endodontic sealers (MTA Fillapex, Sealapex, and AH Plus) to root canal dentin. Sixty slices of extracted human canines were obtained from cervical, middle, and apical root thirds. Root canals were standardized and specime
Braz. oral res.. Publicado em: 24/01/2014