1. Heterogeneous Fenton-like catalytic degradation of phenazine dye over CeO2 (CP-2) nanoscale powder
Abstract A heterogeneous Fenton-like process was explored for oxidation of phenazine dye using ceria polishing material (CP-2). XRD, SEM, FTIR, UV-vis DRS, and pHPZC techniques were applied to characterize the catalyst features. The performance of the heterogeneous Fenton-like process was investigated under various parameters (reaction time, pH, H2O2 concent
Cerâmica. Publicado em: 2022
-
2. Synthesis, Characterization, and Photocatalytic Properties of Flower-like Mn-doped Ceria
Mn-doped CeO2 flower-like microstructures have been synthesized by a facile one-step composite-hydroxide-mediated method. The structure, morphology, optical and the surface properties of Mn doped CeO2 have been investigated by X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM), UV-Vis absorption spectroscopy and X-ray photoelectron
Mat. Res.. Publicado em: 16/07/2018
-
3. Efeitos da dopagem com gadolínia na densificação e nas propriedades elétricas de soluções sólidas Ce0,99-xGdxCu0,01O2-δ
Resumo Soluções sólidas à base de céria (CeO2) são materiais promissores para aplicação como eletrólitos de células a combustível de óxido sólido. Apesar das boas propriedades elétricas, um dos principais inconvenientes destes materiais são as altas temperaturas de sinterização (normalmente acima de 1400 °C) necessárias para completa densi
Cerâmica. Publicado em: 2017-12
-
4. Electrical and microstructural characterization of Gd-doped Ceria/Y-doped Zirconia bi-layer electrolyte prepared by tape casting
ABSTRACT GDC-YSZ bi-layer SOFC electrolytes are an interesting manner to protect GDC electrolytes of the low oxygen partial pressure present at anode-electrolyte interface. This oxygen partial pressure condition and high temperatures during the operation of SOFC permit GDC electrolyte reduction injuring the performance of SOFC. In this work, GDC-YSZ bi-layer
Matéria (Rio J.). Publicado em: 22/05/2017
-
5. Síntese em uma etapa e microestrutura de compósitos CuO-SDC
Resumo Uma rota de síntese em uma etapa baseada no método dos precursores poliméricos foi usada para produzir pós do nanocompósito contendo as fases CuO e céria dopada com samária (SDC). Esta rota química permitiu obter pós compósitos com reduzido tamanho de partícula e uniforme distribuição dos elementos Cu, Ce e Sm. O material particulado foi
Cerâmica. Publicado em: 2017-03
-
6. The Effect of Co and Zn Addition on Densification and Electrical Properties of Ceria-Based Nanopowders
Abstract In this work, cobalt and zinc-doped Ce0.8Gd0.2O1.9 samples were prepared starting from a commercial nanopowder and compared to the undoped material. The powder samples were pressed and afterwards sintered by a two-step procedure, before characterization by X-Ray Diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Scanning Electron Microscopy
Mat. Res.. Publicado em: 11/08/2016
-
7. Nickel / Doped Ceria Solid Oxide Fuel Cell Anodes for Dry Reforming of Methane
Neste trabalho, foi estudado o desempenho catalítico de materiais a base de Ni, suportado em cério dopado com Zr, Pr e Nb para serem usados como anodos em células a combustível de óxido sólido (SOFC) alimentadas com combustíveis contendo metano e CO2. Os anodos foram preparados pelo método hidrotérmico, usando um teor de Ni (14% em volume) menor do
J. Braz. Chem. Soc.. Publicado em: 2014-12
-
8. Catalytic oxidation of volatile organic compounds (n-hexane, benzene, toluene, o-xylene) promoted by cobalt catalysts supported on γ-Al2O3-CeO2
Cobalt catalysts supported on γ-alumina, ceria and γ-alumina-ceria, with 10 or 20%wt of cobalt load, prepared by the wet impregnation method and characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), field emission transmission electron microscopy (FETEM), N2 adsorption-desorption isotherms (BET/BJH methods), energy-dispersive X-ray
Braz. J. Chem. Eng.. Publicado em: 2014-09
-
9. Efeito da adição de óxido de cobalto na sinterização e propriedades elétricas da cerâmica Ce0,8Gd0,2O1,9 obtida a partir de nanopós
Células a combustível de óxido sólido é uma tecnologia promissora de geração de energia limpa e utilizam zircônia estabilizada com ítria como eletrólito. Devido à alta temperatura de operação convencional, a busca por novos materiais de eletrólito tem sido feita e apontam a céria como um substituto. Entretanto, pós micrométricos de céria de
Cerâmica. Publicado em: 2014-06
-
10. Microestrutura e condutividade elétrica do eletrólito sólido de céria-20% mol gadolínia com adições de SrO, TiO2 e SrTiO3
Os efeitos da adição de SrO, TiO2 e SrTiO3 na sinterização, na microestrutura e na condutividade elétrica do eletrólito sólido céria-gadolínia foram sistematicamente investigados. Foram preparadas pelo método convencional de mistura dos reagentes de partida seguida de reação em estado sólido composições contendo 1, 2,5 e 5% mol dos aditivos. D
Cerâmica. Publicado em: 2013-12
-
11. Estudo do crescimento de nanofitas de céria dopada com gadolínio por sistema de aquecimento por micro-ondas
O óxido de cério (céria) tem atraído atenção devido às suas importantes aplicações, como em células a combustível de óxido sólido, catalisadores de gases de exaustão de automóveis, catalisadores para a obtenção de hidrogênio, bloqueadores de raios ultravioleta, biomateriais, entre outros. Controlar os métodos de síntese da céria é de gr
Cerâmica. Publicado em: 2013-09
-
12. Condutividade elétrica de CeO2-10 mol% Gd2O3 - x mol% Sm2O3 (0 < x < 2)
A condutividade elétrica de CeO2-10 mol% Gd2O3 co-dopado com x mol% de Sm2O3 (0 < x < 2) foi investigada. O aumento da concentração total de dopantes com a co-dopagem não promoveu variação significativa do parâmetro de rede e do tamanho médio de grão. A adição de até 1,0% em mol de co-dopante favoreceu a condutividade elétrica do grão e acima d
Cerâmica. Publicado em: 2013-06