Wear behavior of Diamond-like Carbon Deposited on Ti6Al4V Prepared with Surface Mechanical Attrition Treatment
AUTOR(ES)
Oliveira, Luciane Yumi Suzuki de
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
21/01/2019
RESUMO
Surface modification by deposition of hard coatings is a way to overpass the poor wear resistance of some metallic materials and one potential material is the Diamond-Like Carbon (DLC). We investigated the wear behavior, and the adhesion of the DLC deposited on a Ti6Al4V (Ti64) alloy after Surface Mechanical Attrition Treatment (SMAT). The SMAT was applied using 100Cr6 steel balls, and the DLC was deposited through the sputtering method. The nano-hardness was evaluated using a MTS Nano Indenter XP. The adhesion of the DLC was evaluated using a CSM Revetest, and the wear tests was performed in a reciprocating linear tribometer from CSM Instruments. The mean wear rate for the Ti64 was 437x10-6 mm3/N/m against 5x10-6 mm3/N/m for the Ti64+SMAT+DLC. The SMAT reduced the wear rate of the DLC coating, showing that the SMAT might be a viable treatment with promising results regarding the DLC wear resistance.
Documentos Relacionados
- Tribocorrosão da liga Ti6A14V, liga nitretada, Ti6A14V revestida por filmes Diamond-Like Carbon (DLC) e obtenção eletroquímica de filmes DLC
- Adherent diamond-like carbon coatings on metals via PECVD and IBAD
- Analyses of Biofilm on Implant Abutment Surfaces Coating with Diamond-Like Carbon and Biocompatibility
- Surface Modification of Ti6Al4V Alloy by Pulsed Lasers: Microstructure and Hydrophobic Behavior
- Influência de parafusos recobertos com Diamond-like carbon (DLC) na interface pilar UCLA/implante