Titanium bioactivity surfaces obtained by chemical/electrochemical treatments

AUTOR(ES)
FONTE

Matéria (Rio J.)

DATA DE PUBLICAÇÃO

2014-03

RESUMO

There are various surface treatments used to modify titanium surfaces to render it bioactive. In this study commercially pure titanium surfaces (cp Ti), grade 2 were modified by acid etching (AE) and anodic oxidation (OA) in order to evaluate the bioactivity in vitro of these surfaces using the simulated body fluid (SBF). The AE was realized using a mixture of acids and AO using 1 mol.L-1 sulfuric acid. The anodic films were obtained under potentiostatic mode, during 60s using as anode a bar of titanium. All the surfaces that means cp Ti, AE and AO were analyzed concerning to morphology, rugosity, structural changes before in vitro bioactivity tests. It was observed by scanning electron microscopy (SEM) that all surfaces presented different morphologies: those with AE showed a surface with peaks and rounded valleys, with Ra = (564±80) nm, the oxidized surfaces with sulfuric acid showed a morphology with small pores uniformly distributed over the surface and Ra = (177±0,02) nm. X-rays diffraction results showed the presence of titanium hydride on the samples with AE and the anatase and rutile phases on the anodic films after heat treatment at 600°C/1h. Bioactivity tests in vitro using SBF at 37°C showed that small aggregates containing Ca and P were observed on surfaces with AE after 30 days soaked in SBF and the surfaces oxidized were fully coated with an apatite layer, identified by SEM.

Documentos Relacionados