The influence of finishing and polishing procedures on dentin bond strength of resin composite and at the interface enamel/restoration / Influência do acabamento e polimento de resina composta na resistência adesiva à dentina e no ângulo cavo-superficial em esmalte
AUTOR(ES)
Diego Ferreira Regalado
DATA DE PUBLICAÇÃO
2007
RESUMO
The objective of this study was to verify the influence of finishing and polishing procedures on dentin bond strength of resin composite, and at the interface tooth/restoration using MEV. Recently extracted human third molars were utilized in this study, after approved by ethics and search committee at FOB-USP. The teeth were restored with Solobond M (VOCO) adhesive system and resin composite Grandio (VOCO) and randomized in the follow groups: G1 (control) - no polishing and finishing, G2 - immediate polishing and finishing procedures, G3 - no polishing and finishing and stored for seven days e G4 - polishing and finishing procedures after seven days under water at 37oC. Sticks 1mm x 1mm were obtained and the bonds were then stressed to failure by microtensile forces in a EMIC universal testing machine at a crosshead speed of 0.5 mm/min. Twenty human third molars were prepared with four cavities with 1mm diameter and 3mm height and restored with the same restoration system used for the microtensile tests and were distributed at the same groups and the interface tooth/restoration was analyzed in MEV by three examinators. The means of bond strength (MPa) and respective standard deviation were: G1 - 23.05 (8.62); G2 - 17.34 (6.11); G3 - 21.64 (7.63) e G4 - 18.12 (6.51). The data were analyzed by One-Way Anova and e Fisher´s test. It was possible to conclude that the finishing and polishing procedures of resin composite decrease significantly the bond strength to dentin of the composite restorations. The Kruskal- Wallis test aplicated to gap scores at the tooth/restoration interface allows to determinate that the finishing and polishing procedures of resin composite do not interfere in gap formation.
ASSUNTO(S)
resistência adesiva acabamento e polimento resin composite polishing and finishing bond strength resina composta
Documentos Relacionados
- Influência do sistema adesivo e do envelhecimento na resistência ao cisalhamento da interface dentina humana-resina composta
- Study of the parameters for microhardness test on dentin and enamel bovines, composite resin and amalgam
- Resistência adesiva dos cimentos resinosos convencionais e autoadesivos à dentina contaminada por saliva
- Avaliação da resistência de união de restaurações de resina composta com diferentes sistemas adesivos, em dois tempos de armazenamento = Composite resin bond strength with different dentin-bonding agents in two storage times
- AVALIAÇÃO DA RESISTÊNCIA DE UNIÃO DE DIFERENTES SISTEMAS DE CIMENTAÇÃO ADESIVA AO ESMALTE E A DENTINA