The Effect of Hydrothermal Treatment on the Morphologies and Optical Properties of Upconversion NaYF 4:Ln 3+ Crystals
AUTOR(ES)
Calil Júnior, Marcos A., Melo, Átila A. C., Rodrigues, Emille M., Sigoli, Fernando A., Rodrigues, Marcelo O.
FONTE
J. Braz. Chem. Soc.
DATA DE PUBLICAÇÃO
2017-09
RESUMO
This work deals with the synthesis and characterization of upconversion NaYF4:Ln3+ crystals. Co-precipitation and hydrothermal methods were used to synthesize NaYF4:Ln3+ crystals. The experimental procedures were modified to obtain crystals in the cubic (α) phase, hexagonal (β) phase or a mixture between cubic and hexagonal (α/β) phases. Reaction temperature was maintained at 200 °C and the time of hydrothermal treatments were maintained at 24 and 48 h. The average diameter of the crystals ranged from 25 nm to 6.4 µm, depending on the chosen synthetic route. These materials can be applied in areas such as photodynamic therapy and bioimaging.
Documentos Relacionados
- Green Synthesis of Upconverting NaYF4 and NaGdF4 Materials and Energy Levels Determination
- Effects of Heat Treatment and Yb 3+ Concentration on the Downconversion Emission of Er 3+ /Yb 3+ Co-Doped Transparent Silicate Glass-Ceramics
- AgAu Nanotubes: Investigating the Effect of Surface Morphologies and Optical Properties over Applications in Catalysis and Photocatalysis
- Growth and optical properties of Cr3+ doped GdAlO3 single crystals
- Effect of Capping Agent on the Morphology, Size and Optical Properties of In2O3 Nanoparticles