Tensile Armor Wires Submitted to Slow Strain Rate Tests in a Corrosive Environment and Cathodic Protection: a Comparison Between Two Different Microstructures

AUTOR(ES)

Tagliari, Mariana dos Reis

FONTE

Mat. Res.

DATA DE PUBLICAÇÃO

06/05/2019

RESUMO

Tensile armor in flexible pipes consists of two or more layers of steel wires. Damage to the outer sheath may cause ingress of seawater in the annular space and thus corrosion of the armor wires. This work focused on the susceptibility of these wires to stress corrosion cracking (SCC) and hydrogen embrittlement (HE) using a slow strain rate test (SSRT) under a bending load in an environment that contains chlorides. The behavior of two different microstructures was compared: martensite and pearlite plus ferrite. Furthermore, the materials were mechanically and metallurgically characterized. The results indicate that martensitic steel is more sensitive to both hydrogen embrittlement and stress corrosion cracking than pearlitic-ferritic steel.

Documentos Relacionados

• ON BRIDGMAN'S OBSERVATIONAL RELATIONSHIP BETWEEN THE RATIO a/R AND THE NATURAL STRAIN IN TENSILE TESTS ON STEEL CYLINDERS*
• Tensile Strength of Glass Fiber Posts Submitted to Different Surface Treatments
• STUDIES IN LEAD POISONING: Comparison between different Laboratory Tests
• Microstructures and Tensile Mechanical Properties of Consolidated Copper
• Platelet antibodies identification: comparison between two laboratory tests