Synthesis and Characterization of CuNb2O6 from an Oxalic Precursor Via Solid State Reaction
AUTOR(ES)
Souto, Maria Veronilda Macedo, Lima, Maria José Santos, Barbosa, Cleonilson Mafra, Gomes, Uilame Umbelino, Souza, Carlson Pereira de, Araújo, Camila Pacelly Brandão de
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
07/07/2016
RESUMO
The present paper's objective was to synthesize and characterize both the oxalic niobium precursor (NH4)3NbO(C2O4)3.H2O, and the product of its doping with Cu and calcining, CuNb2O6. In order to obtain the niobium precursor, commercially available niobium oxide (Nb2O5) was subject to fusion with potassium bisulfate (KHSO4). Once leached with water, the powder was complexed with oxalic acid and ammonium oxalate. The as produced material was manually mixed with copper nitrate Cu(NO3)2.2H2O (25% Cu molar) and calcined at 1000°C in a muffle furnace. CuNb2O6 was then obtained. The precursor was characterized by XRD, SEM, FT-IR, XRF, TG/DTG. The calcination product was characterized by XRD, XRF and SEM. Results show that single phase CuNb2O6 could be obtained by this method without Nb2O5 contamination.
Documentos Relacionados
- Synthesis and Characterization of Niobium Carbide with Copper Addition Obtained Via Gas Solid Reaction
- Fios supercondutores de Cu-Nb3Sn preparados pelo metodo sinterização na fase liquida do cobre, com o uso de Nb-H
- The synthesis of oligoribonucleotides containing N6-alkyladenosines and 2-methylthio-N6-alkyladenosines via post-synthetic modification of precursor oligomers
- Síntese e caracterização de catalisadores VOx/Nb2O5/Al2O3 para a reação de desidrogenação oxidativa de parafinas lineares
- Synthesis of guanidine from ammonium thiocyanate in solid state