Synthesis and applications of polystyrene-block-poly(N-vinyl-2-pyrrolidone) copolymers






Abstract This work describes the synthesis and applications of amphiphilic polystyrene-block-poly(N-vinyl-2-pyrrolidone) (PS-b-PVP) copolymers as a silver and silica nanoparticle surface modification agent. The synthesis of PS-b-PVP was carried out using controlled/living radical polymerization techniques. The synthesis of the block copolymers was confirmed by gel permeation chromatography and hydrogen nuclear magnetic resonance, presenting a polydispersity index of around 1.4 and number average molecular weight ranging between 10,000-14,000 g mol-1. The PS-b-PVP copolymers were applied as a silver nanoparticle (AgNP) stabilizing agent. These nanoparticles were produced by a single step and presented an 11 ± 1 nm diameter. Furthermore, the PS-b-PVP copolymers were also applied as a silica nanoparticle (SiO2NP) surface modification agent. The SiO2NP were synthesized by the Stöber method presenting a 72 ± 9 nm diameter. The SiO2NP surface modification by adsorption of PS-b-PVP caused the formation of a 5 ± 1 nm thick polymeric layer, providing the SiO2NP with a hydrophobic surface character. The structural and chemical characteristics shown by PS-b-PVP copolymers highlights their versatility for several applications, such as: water-in-oil emulsifier, stabilizing or coupling agents between inorganic particles and polymeric matrices.

Documentos Relacionados