Synergistic Effect of EG and Cloisite 15A on the Thermomechanical Properties and Thermal Conductivity of EVA/PCL Blend
AUTOR(ES)
Tsotetsi, Tebello Abel, Mochane, Mokgaotsa Jonas, Motaung, Tshwafo Elias, Gumede, Thandi Patricia, Linganiso, Zikhona Linda
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
01/12/2016
RESUMO
The purpose of this study was to investigate the synergy of expanded graphite (EG) and Cloisite 15A (C15A) on the thermal conductivity and thermomechanical properties of ethylene-vinyl acetate copolymer/poly ( ɛ-caprolactone) (EVA/PCL) blend. Scanning electron microscopy (SEM) results showed that the blend had a phase separation, in which the PCL phase (appeared as droplets) was dispersed uniformly in the EVA matrix in all samples. The results from SEM and X-ray diffraction (XRD) showed that as the EG content increases, graphite sheets increase, leading to a high probability of re-stacking and poor dispersion as well, however the synergy rendered an increase in the storage modulus for the composite containing low content of EG (5phr) in both the EG and clay containing samples. The addition of EG showed a slight increase in thermal stability,but the presence of C15A decreased the onset of degradation of EVA/PCL blend. However, at high temperatures the synergistic effect of EG and C15A showed better thermal stability for EVA/PCL blend than EG alone. The addition and increase in EG content improved thermal conductivity of the EVA/PCL blend in both the clay containing and EG containing samples, however the clay-containing samples showed lower values compared to EG only.
Documentos Relacionados
- The Effect of Rapid Microwave Sintering Process on the Electrical Conductivity, Thermal Conductivity and Mechanical Properties of Al-TiC Composites
- Solid state polymerization of pet/pc extruded blend: effect of reaction temperature on thermal, morphological and viscosity properties
- Study on mechanical & thermal properties of PCL blended graphene biocomposites
- Effect of quinoa and potato flours on the thermomechanical and breadmaking properties ofwheat flour
- The effect of reinforcement volume ratio on porosity and thermal conductivity in Al-Mgo composites