Synergistic Effect of 4A Zeolite from Rice Husk Ash without Aging Time and Silane on the Adhesion Properties of a Warm Mix Asphalt

AUTOR(ES)

Arroyo-Martínez, Paula C., Sánchez-Flores, Norma A., Villafuerte-Castrejón, María E., Vivar-Ocampo, Rodrigo

FONTE

J. Braz. Chem. Soc.

DATA DE PUBLICAÇÃO

2018-01

RESUMO

4A Zeolite was synthesized using rice husk ash (RHA) as a raw material in a microwave-assisted hydrothermal synthesis. Two new procedures were proposed: procedure A, using RHA as the raw material, and procedure B, using the depolymerized RHA. Both procedures were performed using microwave-assisted hydrothermal synthesis, and neither synthesis required an aging time. Crystallinities of over 90 and 80% were reached at 100 ºC after 30 min of microwave heating for procedures A and B, respectively. The obtained zeolites were used as warm mix asphalt additives, and the performance of the zeolite obtained from procedure A was better. Additionally, the zeolite obtained from procedure A and commercial silane were used separately as asphalt-aggregate adhesion promoter. An increase in the adhesion percentage from 30% of a blank sample to 94% was observed.

Documentos Relacionados

• Properties of silica from rice husk and rice husk ash and their utilization for zeolite y synthesis
• Hydro-Physical Properties of a Typic Hapludult under the Effect of Rice Husk Ash
• Mixing process influence on thermal and rheological properties of NBR/SiO2 from rice husk ash
• Study on properties of rice husk ash and its use as cement replacement material
• Production of silica gel from residual rice husk ash