Study on Effect of EAFD Particulate Reinforcement in AA7075 Aluminum Matrix Composites
AUTOR(ES)
Alves, Elizeth Oliveira, Amaro, Daniel Ricardo Araújo, Silva, Enéas Carlos de Oliveira, Araújo Filho, Oscar Olimpio de, Alves, Kleber Gonçalves Bezerra
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
13/09/2018
RESUMO
Eletric arc furnace dust is dangerous solid waste that is generated in steel manufacturing processes. The utilization of the dust from these industries avoids disposing it into industrial waste landfills and saves costs. In this study, an attempt has been made to fabricate aluminum matrix composites reinforced with EAFD particulate, throught the conventional powder metallurgy technique. Al-5%EAFD proposed was then compared to the AA7075 alloy, manufactured under the same conditions. According to the results obtained, the addition of EAFD into aluminum matrix resulted in increased microhardness values and had significant contributuion to improve Storage modulus compared with the base metal. The reinforcement particle was uniformly dispersed into the matrix and intermetallic phases were not observed in the content of waste blended into the composite.
Documentos Relacionados
- Avaliação da tixoconformabilidade das ligas AA7075 a AA7004
- EValuation of the thixoformability of AA7004 and AA7075 alloys
- Effect of Preheating on Microstructure and Tensile Properties of Friction Stir Welded AA7075 Aluminium Alloy Joints
- Effects of Aging Temperature, Time, and Pre-Strain on Mechanical Properties of AA7075
- Caracterização microestrutural das ligas AA7004 e AA7075 tixoforjadas em prensa excêntrica