Síntese e caracterização de perovskitas LaNi(1-x)Co xO3 como precursores de catalisadores para a conversão do metano a gás de síntese pela reforma com CO2
AUTOR(ES)
Lima, Sania Maria de, Assaf, José Mansur
FONTE
Química Nova
DATA DE PUBLICAÇÃO
2007-04
RESUMO
LaNiO3 perovskite was modified by partial substitution of nickel by cobalt in order to increase the stability and resistance to carbon deposition during the methane CO2 reforming. The results showed that a suitable combination of precipitation and calcination steps resulted in oxides with the desired structure and with important properties for application in heterogeneous catalysis. The partial substitution of Ni by Co resulted in lower rates of conversion of both the reactants, but the catalyst stability was highly increased. The LaNi0.3Co0.7O3 catalyst, calcined at 800 ºC, was the most active under the reaction conditions.
Documentos Relacionados
- Synthesis and Characterization of LaNiO3, LaNi(1-x)Fe xO3 andLaNi(1-x)Co xO3 Perovskite Oxides for Catalysis Application
- Síntese e caracterização de perovskitas do tipo LaNi1-xCu xO3 para a purificação de hidrogênio para PaCOS
- Síntese de catalisadores do tipo LaNixFe1-xO3 como precursores catalíticos para reação oxidação parcial do metano
- Conversão de biogás em gás de síntese via reações de reforma do metano com CO2 e a vapor sobre catalisadores de Ni-Y-Al
- Síntese e caracterização de perovskitas LaMnO3 e γ-alumina como catalisadores para a reação de combustão do metano