Síntese e caracterização de CaZrO3 e BaZrO3 nanoestruturados
AUTOR(ES)
Ibiapino, Amanda Laura, Figueiredo, Laysa Pires de, Lascalea, Gustavo E., Prado, Rogério Junqueira
FONTE
Quím. Nova
DATA DE PUBLICAÇÃO
2013
RESUMO
In this work, nanostructured samples of barium zirconate (BaZrO3) and calcium zirconate (CaZrO3) were synthesized by the gel-combustion method, using glycine as fuel. The ceramic powders were calcined at 550 °C for 2 h and subsequently heat treated at 1350 °C for 10 min (fast-firing). The X-ray diffraction technique was employed to identify and characterize the crystalline phases present in the synthesized powders, using the Rietveld method. Monophasic nanostructured samples of BaZrO3 and CaZrO3 presenting average crystallite sizes of around 8.5 and 10.3 nm, respectively, were found after fast-firing.
Documentos Relacionados
- Síntesis en medio poli-alcohólico y caracterización de Perovskitas BaHfO3 y BaZrO3
- Pós nanométricos de BaZrO3: preparação e caracterização de cerâmicas
- Structural and magnetic properties of YBa2Cu3O7/BaZrO3 composites
- Síntese e caracterização de cerâmicas ferroelétricas de BaTiO3 modificadas com Sm3+
- Síntese, caracterização e aplicações de fotocatalisadores de TiO2 nanoestruturados