Selective Surfaces of Black Chromium for Use in Solar Absorbers

AUTOR(ES)

Nunes, Rogério Antônio Xavier, Costa, Vilma Conceição, Sade, Wagner, Araújo, Frederico Resende, Silva, Guilherme Marconi

FONTE

Mat. Res.

DATA DE PUBLICAÇÃO

09/11/2017

RESUMO

One of the applications of selective surfaces is to improve performance of solar absorbers. The purpose of this work is to produces selective coatings with high absorption of solar radiation in the range of UV/Vis/NIR. It was prepared a selective surface composed of black chromium (Cr/Cr2O3) deposited on substrates of AISI 304 stainless steel using the technique of electrolytic deposition for application in solar thermal absorbers. The great parameters for deposition consisted of a continuous electric current of 2A for 90s, at a constant temperature of 40°C. After deposition, the samples under went to a heat treatment at 600°C for 2h for oxidation. The coatings thicknesses were determined. From the SEM analysis coupled with EDS, it was found that the microstructures reported sample of cermets. The XRD results show diffraction peaks related to metallic chromium (Cr) and chromium oxide (Cr2O3). Spectral absorptance values more 90.0% were found.

Documentos Relacionados

• Selective Solar Surface Solar Based on Black Chromium: Influence of Electrodeposition Parameters in the Absorption of Surfaces
• Evaluation of Potential Residual Silica as Antireflective Layer for Selective Solar Surface of Black Chromium
• SOLAR COLLECTORS, SELECTIVE SURFACES, AND HEAT ENGINES
• Theoretical Approach to Simulate Efficient Selective Solar Absorbers With Micro or Nano Structured Arrays
• Estudo Comparativo de SuperfÃcies Seletivas para Coletores Solares