Resistência mecânica de hidrogéis termo-sensíveis constituídos de Alginato-Ca2+ / PNIPAAm, tipo Semi-IPN
AUTOR(ES)
Campese, Gilsinei Marques, Tambourgi, Elias Basile, Guilherme, Marcos Rogério, Moura, Márcia Regina de, Muniz, Edvani Curti, Youssef, Elza Youssef
FONTE
Química Nova
DATA DE PUBLICAÇÃO
2007
RESUMO
Thermosensitive hydrogels were synthesized using alginate-Ca2+ in association with a thermosensitive polymer, such as PNIPAAm. The mechanical properties of the hydrogels were determined measuring the maximum tension of deformation. With the increase of the temperature by 25 to 40 ºC above the LCST the chains of PNIPAAm collapsed, dragging the alginate net and diminishing the size of the pores. The decrease in the size of the pores of the hydrogel was followed by an increase in the mechanicals resistance of the material.
Documentos Relacionados
- Hidrogéis semi-IPN baseados em rede de alginato-Ca2+ com PNIPAAm entrelaçado: propriedades hidrofílicas, morfológicas e mecânicas
- Morfologia de hidrogéis-ipn termo-sensíveis e ph-responsivos para aplicação como biomaterial na cultura de células
- Proton conductive membranes based on poly (styrene-co-allyl alcohol) semi-IPN
- Caracterização de hidrogéis condutores constituídos por PAAm e PEDOT/PSS por meio de planejamento fatorial
- Efeito do tipo de cimento na resistência mecânica de argamassas de escoria de cobre