Release Behavior of Arsenic during Pyrolysis of Two Chinese Coal Gangues

AUTOR(ES)

Cao, Yanzhi

FONTE

J. Braz. Chem. Soc.

DATA DE PUBLICAÇÃO

16/09/2019

RESUMO

Release behaviors of arsenic (As) during pyrolysis of two Chinese coal gangues were studied in this report. The pyrolysis experiments were carried out in a temperature programmed tube furnace under N2 atmosphere with different temperature (200-1200 ºC), residence time (0-50 min), heating rate (10-50 ºC min-1) and N2 gas flow rate (100-500 cm3 min-1). The experiment results, under different pyrolysis conditions, indicate that the release ratio of As increases with increasing temperature, as well as residence time during pyrolysis of coal gangues. Besides that, higher heating rate during pyrolysis of coal gangues can stimulate the As release from coal gangue to some extent. The release ratio of As increases to a maximum and then decreases when the N2 gas flow rate is increased. The results imply that different modes of ocurrence of As exist in two coal gangues. The As release has positive relation with the volatile matter release. As is more easily released than coal gangue matrix during coal gangue pyrolysis.

Documentos Relacionados

• Electrical Behavior of Carbon Fiber/Phenolic Composite during Pyrolysis
• CoAl2O4 blue nanopigments prepared by liquid-feed flame spray pyrolysis method
• Behavior of Eucalyptus grandis and E. cloeziana seedlings grown in arsenic-contaminated soil.
• Release of two vasodilators, adenosine and prostacyclin, from isolated rabbit hearts during controlled hypoxia.
• AIDS activist mum after release from Chinese prison