PROPRIEDADES MECÂNICAS E TRIBOLÓGICAS DE AÇO AUSTENÍTICO 304 SUBMETIDO À NITRETAÇÃO POR: IMPLANTAÇÃO IÔNICA E IMPLANTAÇÃO IÔNICA POR IMERSÃO EM PLASMA.
AUTOR(ES)
Andressa Cristiane Zaika
DATA DE PUBLICAÇÃO
2007
RESUMO
The aim of this work is to characterize the mechanical and tribological properties of AISI 304 austenitic stainless steel submitted to N+ ion implantation and Nitrogen plasma immersion ion implantation (PI3). The ion implantation conditions were to obtain a plateau distribution of N íons in atomic concentrations of up to 27. The PI3 nitretation were performed at temperatures up to 400C for 4 h. The samples were characterized by q-2q X-ray diffraction in Bragg-Bretano condition, scanning electron microscopy, X-ray energy dispersive spectroscopy and optical microscopy. The hardness and elastic modulus were obtain by using the nanoindentation technique. The tribological properties were measured by a linear reciprocating tribometer, with spheres of 100Cr6 and WC(Co), with loads up to 12 N. The results compare the mechanical properties of ion implanted samples with those submitted to PI3. The hardness of the highest ion implanted dose (27) is equivalent to the sample nitrided by PI3 at 387C for 4 hs. The wear rate of the ion implanted samples increases with dose. For the PI3 samples, the wear rate decreases with increasing time and temperature of the nitriding process.
ASSUNTO(S)
nitretação fisica dureza implantação ionica módulo elástico plasma aço inoxidável
ACESSO AO ARTIGO
http://www.bicen-tede.uepg.br/tde_busca/arquivo.php?codArquivo=121Documentos Relacionados
- AÇO DUPLEX LDX 2101 SUBMETIDO À NITRETAÇÃO POR IMPLANTAÇÃO IÔNICA, IMPLANTAÇÃO IÔNICA POR IMERSÃO EM PLASMA E DESCARGA LUMINOSA: PROPRIEDADES MECÂNICAS E TRIBOLÓGICAS
- Nitrocarbonetação por plasma, em potencial flutuante, de aço inoxidável austenítico AISI 304
- Deposição de filmes de carbono tipo diamante sobre substratos metálicos por meio da técnica de implantação iônica por imersão em plasma.
- Implantação iônica por imersão em plasma em materiais metálicos leves
- Implantação iônica por imersão em plasma em materiais metálicos leves