Proposição de um Modelo Empírico para Determinação das Temperaturas Críticas Durante Resfriamento Contínuo em Zonas Termicamente Afetadas de Aços IF Soldados pelo Processo TIG

AUTOR(ES)

Cezário, Ana Luiza Soares

FONTE

Soldag. insp.

DATA DE PUBLICAÇÃO

23/09/2019

RESUMO

Resumo Aços IF são amplamente empregados na indústria automobilística. No decorrer das aplicações de soldagem, eles passam pela transformação de fase austenita (γ) → ferrita (α) que ocorre por nucleação e crescimento de grão e, em condições isotérmicas, é descrita pela equação JMAK. Todavia, as transformações de fases pós-soldagem acontecem a partir de resfriamento contínuo. Assim, o presente trabalho caracterizou a cinética de transformação γ → α e propôs um modelo empírico para prever as temperaturas críticas durante o resfriamento contínuo em zonas termicamente afetadas de três tipos de aços IF. Amostras dos aços foram submetidas a ensaios dilatométricos com diferentes taxas de resfriamento contínuo. Determinaram-se as temperaturas críticas de transformação de fase (γ→α) e obteve-se uma equação empírica que correlacionou a temperatura crítica com a taxa de resfriamento e que viabilizou a previsibilidade da cinética de transformação de fases. Processo de soldagem TIG mecanizado foi aplicado nos aços IF com monitoramento de ciclos térmicos e, em regiões da ZTA com condições de austenitização e taxa de resfriamento similares às utilizadas nos ensaios dilatométricos, verificou-se que a equação empírica obtida é uma alternativa viável para prever as temperaturas críticas e a microestrutura durante o resfriamento contínuo na ZTA destes materiais. Abstract IF steels are widely used in the automotive industry. In the course of the welding applications, they undergo the transformation of austenite (γ) → ferrite (α) phase that occurs by nucleation and grain growth and, under isothermal conditions, is described by the JMAK equation. However, post-weld phase transformations occur under continuous cooling conditions. Thus, the present work characterized the transformation kinetics γ → α and proposed an empirical model to predict critical temperatures during continuous cooling in heat affected zones of three types of IF steels. Samples of the steels were submitted to dilatometric tests with different rates of continuous cooling. The critical phase transformation temperatures (γ → α) were determined and an empirical equation was obtained which correlated the critical temperature with the cooling rate, which enabled the predictability of phase transformation kinetics. Mechanized TIG process was applied to IF steels with thermal cycling monitoring and, in regions of the HAZ with austenitizing conditions and cooling rates similar to those used in the dilatometric tests, it was verified that the obtained empirical equation is a viable alternative to predict the critical temperatures and the microstructure during the continuous cooling in the HAZ of these steels.

Documentos Relacionados

• Avaliação das tensões residuais em tubos de pequeno diâmetro soldados pelo processo TIG orbital
• Influencia do insumo de calor na corrosão interglanular dos aços AISI-316 soldados pelo processo MIG
• Determinação das Temperaturas Cardinais de Frutos de Cajueiros Utilizando um Modelo Não Linear de Desenvolvimento
• Resistência à corrosão de junta dissimilar soldada pelo processo TIG composta pelos aços inoxidáveis AISI 316L e AISI 444
• Proposta de roteiro para a determinação das variáveis de soldagem do Processo TIG pulsado aplicado à soldagem de chapas finas