Properties of experimental resins based on synthesized propoxylated bis-GMA with different propionaldehyde ratios
AUTOR(ES)
Denis, Aline Bassi, Plepis, Ana Maria Guzzi, Martins, Virginia da Conceição Amaro, Pereira, Jose Carlos, Cilli, Renato, Prakki, Anuradha
FONTE
Materials Research
DATA DE PUBLICAÇÃO
05/04/2012
RESUMO
The effect of different propionaldehyde ratios on the properties of bis-GMA-based comonomers and copolymers diluted with propoxylated bis-GMA (CH3bis-GMA) was evaluated. Five experimental comonomers were prepared combining bis-GMA with CH3bis-GMA and propionaldehyde at 0, 2, 8, 16, 24 mol%. Light polymerization was effected with the use of 0.2 wt. (%) each of camphorquinone and N,N-dimethyl-p-toluidine. Resin degrees of conversion (%DC) were evaluated by FT-IR spectrophotometry and Tg by Differential Scanning Calorimeter. Complex viscosity (η*), the effect of temperature on η*, and Microhardness (H) for dry and wet samples were also determined. Data were analyzed by Student's t-test, one-way ANOVA and Tukey-Kramer test (α = 0.05). The group with 24 mol% additive had a significant increase in %DC and H, and the lowest comonomer Tg and η*. No remarkable variation was noted in copolymers Tg s. All resins presented Newtonian behavior of viscosity, which linearly decreased with increased temperature. The η* decreased sigmoidally as the additive ratio increased.
Documentos Relacionados
- Influência de aditivos nas propriedades de comonômeros, copolímeros e compósitos a base de Bis-GMA, diluído com TEGDMA ou análogos sintetizados do Bis-GMA (CH3Bis-GMA e CF3Bis-GMA)
- Bis-EMA addition influence on physical properties of experimental Bis-GMA/TEGDMA-based resin luting agents
- Water sorption of CH3- and CF3-Bis-GMA based resins with additives
- Apoptosis and survivability of human dental pulp cells under exposure to Bis-GMA
- Factors related to polymerization stress development in experimental composites using BisGMA, TEGDMA and BisEMA