Preparation and characterization of a homemade Josephson junction prepared from a thin film sintered in a domestic microwave oven
AUTOR(ES)
Freitas, Gustavo Quereza, Zadorosny, Rafael, Cena, Cícero Rafael, Silveira, João Borsil, Moreto, Jéferson Aparecido, Carvalho, Claudio Luiz
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
08/03/2016
RESUMO
A homemade Josephson junction was successfully obtained using a superconductor thin film of the BSCCO system. The film was deposited on a lanthanum aluminate, produced from a commercial powder with a nominal composition Bi1.8Pb0.4Sr2CaCu2Ox, was thermally treated by a domestic microwave oven. The XRD analysis of the film indicated the coexistence of Bi-2212 and Bi-2223 phases and SEM images revealed that a typical superconductor plate-like morphology was formed. From the electrical characterization, performed using DC four probes technique, it was observed an onset superconducting transition temperature measured around 81K. At the current-voltage characteristics curve, a step of electric current at zero-voltage could be observed, an indicative that the tunneling Josephson occurred.
Documentos Relacionados
- The solvent free preparation of beta-amino esters alpha,beta-unsaturated ketones and esters with domestic microwave oven
- PREPARATION AND CHARACTERIZATION OF THIN-FILM COMPOSITE REVERSE OSMOSIS MEMBRANE ON A NOVEL AMINOSILANE-MODIFIED POLYVINYL CHLORIDE SUPPORT
- Preparation and characterization of electrodeposited iron + cobalt thin films from a chloride bath
- Inhalation trauma due to overheating in a microwave oven.
- Inhalation trauma due to overheating in a microwave oven