Optimization of the Deposition Parameters of HVOF FeMnCrSi+Ni+B Thermally Sprayed Coatings
AUTOR(ES)
Sucharski, Gustavo Bavaresco, Pukasiewicz, Anderson Geraldo Marenda, Váz, Rodolpho Fernando, Paredes, Ramón Sigifredo Cortés
FONTE
Soldag. insp.
DATA DE PUBLICAÇÃO
2015-06
RESUMO
AbstractHVOF thermal spray process produces coatings with low porosity and low oxide content, as well as high substrate adhesion. Small variations on the parameters of the HVOF process can generate coatings with different characteristics and properties, which also is chemical composition depended of the alloy. FeMnCrSi alloy is a cavitation resistant class of material with a great potential for HVOF deposition use. The main goal of this article is to study the influence of some HVOF parameters deposition, as standoff distance, powder feed rate and carrier gas pressure on three different alloys. FeMnCrSi experimental alloys with some variations in nickel and boron content were studied. Taguchi experimental design with L9 orthogonal array was used in this work. Porosity, oxide content, tensile adhesion strength and microhardness of the coatings were evaluated. The results indicated that all factors have significant influence on these properties. Chemical composition of the alloys was the most important factor, followed by the carrier gas pressure, standoff distance and powder feed rate. The addition of Ni, produces coatings with lower levels of oxide content and porosity. An experiment with improved parameters was conducted, and a great improvement on the coating properties was observed.
Documentos Relacionados
- High Temperature Erosion-oxidation Resistance of Thermally Sprayed Nanostructured Cr3C2-25(Ni-20Cr) Coatings
- Influence of process parameters on the quality of thermally sprayed X46Cr13 stainless steel coatings
- Kinetics Oxidation and Characterization of Cyclically Oxidized Layers at High Temperatures for FeMnSiCrNiCe and FeSiCrNi Alloys
- Effect of Experimental Parameters on Wear Response of Thermally Sprayed Carbide Based Coatings
- Caracterização da resistência à corrosão de ligas inoxidáveis Fe-Mn-Si-Cr-Ni-(Co) com efeito de memória de forma