Microtensile bond strength of CAD/CAM materials to dentin under different adhesive strategies
Bellan, Mariá Cortina, Cunha, Patrícia Fernandes Jerzewski Sotero da, Tavares, Julieta Gomes, Spohr, Ana Maria, Mota, Eduardo Gonçalves
Braz. oral res.
DATA DE PUBLICAÇÃO
Abstract: The present study aimed to evaluate the microtensile bond strength (μTBS) of novel computer-aided design/computer-aided manufacturing (CAD/CAM) restorative materials to dentin using different adhesive strategies. Thirty-two crowns were milled using CAD/CAM materials (Vita Mark II as control, Vita Suprinity, Vita Enamic and Lava Ultimate) and luted to dentin using different resin cements (RelyX ARC, RelyX Unicem 2 and RelyX Ultimate). The specimens were stored in 100% relative humidity at 37°C for 24 h and sectioned. The samples (n = 16) with cross-sectional areas of approximately 0.90 mm2, were submitted to a μTBS test in a universal testing machine with a crosshead speed of 0.5 mm/min. The samples were analyzed with SEM to determinate the failure mode. According to 2-way ANOVA and Tukey's test (α=0.05), the interaction effect (material x luting strategy) was significant (p=0.001). Regardless of the luting strategy, a higher μTBS was obtained with Lava Ultimate and Vita Enamic, which were significantly different from Vita Mark II and Vita Suprinity (p<0.05). For Vita Mark II, Vita Suprinity, Vita Enamic, and Lava Ultimate, the μTBS obtained with RelyX Unicem 2 was not significantly different from that obtained with RelyX ARC or RelyX Ultimate. All groups obtained at least three types of failure. The adhesive strategy with self-adhesive resin cement was comparable to conventional resin cement with total-etch or self-etch adhesive techniques in the bond of novel CAD/CAM materials to dentin.
- ERRATUM: Microtensile bond strength of CAD/CAM materials to dentin under different adhesive strategies. Braz Oral Res. 2017;31:e109.
- Reliability, failure probability, and strength of resin-based materials for CAD/CAM restorations
- Shear bond strength evaluation of metallic brackets bonded to a CAD/CAM PMMA material compared to traditional prosthetic temporary materials: an in vitro study
- Effects of air abrasion with alumina or glass beads on surface characteristics of CAD/CAM composite materials and the bond strength of resin cements
- Reconhecimento de padrões para aplicações em CAD/CAM