Microstructure and tribological properties of cobalt-based Stellite 6 alloy coating by electro-spark deposition
AUTOR(ES)
Jing, QiFeng, Tan, YeFa
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
28/05/2013
RESUMO
The cobalt-based Stellite 6 coating with a thickness of 0.5 mm was deposited onto 45 carbon steel by electro-spark deposition technology. Microstructure, chemical composition, phase composition, microhardness distribution and wear resistance of the coating were researched by a series of experiments. The results indicate that, the coating with refined and compact microstructure is mainly composed of Co, Cr7C3, Co6W6C and CrCo. The coating makes metallurgical bonding interface with the substrate. Microhardness of the coating is improved significantly with an average value of 827.9 HV0.5, which is about 3.6 times that of the substrate. Under the same experimental condition, mass loss of the substrate is about 4.2-4.5 times that of the coating, so the coating shows excellent wear resistance. Main wear mechanism of the coating is abrasive wear at low speed or low load stage, and fatigue wear at high speed or heavy load condition.
Documentos Relacionados
- Microstructure and Properties of Coating of FeAlCuCrCoMn High Entropy Alloy Deposited by Direct Current Magnetron Sputtering
- Microstructure and mechanical properties of Pb-4%Sb alloy processed by equal channel angular pressing
- Microstructure and Properties of Nickel-based C276 Alloy Coatings by PTA on AISI 316L and API 5L X70 Steel Substrates
- Surface Modification of Ti6Al4V Alloy by Pulsed Lasers: Microstructure and Hydrophobic Behavior
- Microstructure, material flow and tensile properties of A356 alloy thixoformed parts