Microstructure and Mechanical Properties of AA6061/AZ31B/AA6061 Composite Plates Fabricated by Vertical Explosive Welding and Subsequent Hot Rolling

AUTOR(ES)

Yang, Wen-wu, Cao, Xiao-qing, Wang, Li-fei, Chen, Zhi-qing, Wang, Wen-xian, Wang, Dong-ya

FONTE

Mat. Res.

DATA DE PUBLICAÇÃO

04/10/2018

RESUMO

In this study, three-ply Al/Mg/Al composite plates were successfully achieved by vertical explosive welding (EXW) method. After EXW, the sound joints were obtained. Then thin three-ply Al/Mg/Al EXWed composite plates with the thickness of 1.78 mm were achieved by hot rolling. The influence of annealing on the interface microstructures and mechanical properties of the thin composite plates was investigated. The results indicated that different morphology with big waveform and mini waveform was present in the explosively bonded interface. The interface shear strength was 91MPa for big waveform side and 92Mpa for mini waveform side. The rolled sample without annealing possessed the high ultimate tensile strength (UTS) value of 235Mpa and elongation of 8.5%. The equiaxed and homogeneous grain morphology of magnesium alloys in the thin three-ply Al/Mg/Al composite plates could be induced by annealing 300°C for 1 h. This contributed to the considerable increase of elongation by 18.5%.

Documentos Relacionados

• Effect of Annealing Process on the Microstructures and Mechanical Properties of AZ31B/A356 Composite Plate Fabricated by Cast Rolling
• Effect of Multi-Pass Bending Deformation on Microstructure Evolution and Mechanical Properties of AZ31 Alloy Sheet
• Effects of Processing Parameters on Microstructure and Mechanical Properties of Powder-Thixoforged SiC p /6061 Al Composite
• Investigation on AA5083/AA7075+Al2O3 Joint Fabricated by Friction Stir Welding: Characterizing Microstructure, Corrosion and Toughness Behavior
• Microwave Sintering of Aluminum-ZrB2 Composite: Focusing on Microstructure and Mechanical Properties