Melting Temperature and Wetting Angle of AlN/Dy2O3 and AlN/Yb2O3 Mixtures on SiC Substrates
AUTOR(ES)
Santos, Aline Corecha, Luz, Ana Paula, Ribeiro, Sebastião
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
2015-10
RESUMO
AbstractThis work aims to evaluate the melting temperature and wetting behavior of AlN/Re2O3 (Re = Dy, Yb) mixtures when in contact with SiC substrates at high temperatures, in order to define whether these compounds can be further used to induce a more effective liquid phase sintering of SiC-based products. The prepared samples were placed on SiC plates and thermally treated up to 1900 °C under argon. The melting point and spreading evolution of different compositions of AlN/Re2O3 on SiC were determined by analyzing images captured as a function of the heating temperature. The contact angle and melting point were measured using the ImageJ software and according to DIN 51730, respectively. Based on the obtained wetting curves, all evaluated conditions resulted in the decrease of the contact angle values with temperature. The mixtures presenting improved wetting (θ ~ 1° and 3°) on SiC plates were the ones above the selected eutectic point.
Documentos Relacionados
- Properties of SiC Ceramics Sintered via Liquid Phase Using Al2O3 + Y2O3, Al2O3 + Yb2O3 and Al2O3 + Dy2O3 as Additives: a Comparative Study
- Efeito do SiC na microestrutura e propriedades de rolos cerâmicos de Al2O3/mulita.
- Estudo da viabilidade de obtenção de cerâmicas de SiC por infiltração espontânea de misturas eutéticas de Y2O3-AlN, Y2O3-Al2O3, R2O3-AlN
- Estudo da influência da adição de polímeros precursores cerâmicos na sinterização de SiC e Al2O3
- Efeito da zircônia na sinterização de SiC com adições de Al2O3 e Y2O3