Mejora de la resistencia al desgaste abrasivo de un revestimiento Fe-Cr-Mn-C mediante la adición de V
AUTOR(ES)
Pérez, Manuel Rodríguez
FONTE
Matéria (Rio J.)
DATA DE PUBLICAÇÃO
20/05/2019
RESUMO
ABSTRACT The aim of this work is to increase the abrasive wear resistance of a coating, applied on plates of AISI 1020 carbon steel, using tubular coated electrodes with the Fe-Cr-Mn-C alloy system. In order to achieve this increase, V was added to the alloy system. The resulting coating were studied using optical microscopy (MO), X-ray diffraction and microhardness tests. Wear tests were carried out in accordance with the procedure of ASTM G 65-B. Results showed that the addition of V to the Fe-Cr-Mn-C system caused significant microstructural modifications, decreasing the amount of martensite in the coating, and increasing the dimensions of the eutectic zone. Also, V originated the formation of VC, in addition to the Cr7C3 carbides present for the two alloy systems. These microstructural modifications provoked that coatings deposited using the Fe-Cr-Mn-V-C alloy system show a significantly higher abrasive wear resistance.
Documentos Relacionados
- Influência da microestrutura na resistência ao desgaste microabrasivo de ligas de F-Cr-C e Fe-Cr-C-Nb
- Desenvolvimento de ligas Fe-C-Cr-(Nb) resistentes ao desgaste
- Processing, microstructural characterization and mechanical properties evaluation of the Al92Fe3Cr2Mn3 alloy
- Caracterização da nova liga Fe-C-Mn-Si-Cr: fragilização da martensita revenida e curvas de revenimento.
- Texture evolution in the Fe-30.5Mn-8.0Al-1.2C and Fe-30.5Mn-2.1Al-1.2C steels upon cold rolling