Mechanical Properties Analysis of Al2024 alloy Submitted to Different Aging Time and different Cold Plastic Deformation degree

AUTOR(ES)

Siqueira, Marcelo Luis

FONTE

Mat. Res.

DATA DE PUBLICAÇÃO

10/07/2019

RESUMO

Brazilian aeronautical industries report that, due to the high mechanical properties presented commercially, AA2024-T351 alloy presents fissures and non-homogeneous deformations during the mechanical processing. This work proposes a manufacturing process capable of increasing the ductility of the material to withstand tensions during processing and a subsequent treatment to recover the mechanical strength of the alloy. The sequence of operations begins with the super-heat treatment at 415ºC 2.5 h, solubilization at 495ºC 2.0 h, mechanical conformation with a degree of area reduction from10% to 90% and artificial aging at 190ºC at times of 2, 4, 6 and 8 hours. The results allowed to obtain an operational sequence where it is possible to form the alloy in the desired component, without loss of mechanical properties and structural defects, in the shortest time possible of heat treatment, reducing the manufacturing costs and increasing productivity.

Documentos Relacionados

• Texture, Microstructure and Mechanical Properties of 6111 Aluminum Alloy Subject to Rolling Deformation
• Microstructural characterization of Ti-6Al-7Nb alloy after severe plastic deformation
• Effect of Multi-Pass Bending Deformation on Microstructure Evolution and Mechanical Properties of AZ31 Alloy Sheet
• Effects of Aging Temperature, Time, and Pre-Strain on Mechanical Properties of AA7075
• Mechanical properties of one and two-step fluoridated orthodontic resins submitted to different pH cycling regimes