Mechanical and microstructural characterization of Nodular Cast Iron (NCI) with Niobium Additions
AUTOR(ES)
Souza, Tânia Nogueira Fonseca, Nogueira, Rogéria Alves Perilo Sousa, Franco, Francis José Saldanha, Aguilar, Maria Teresa Paulino, Cetlin, Paulo Roberto
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
2014-10
RESUMO
Nodular cast irons (NCIs) involve the inoculation and nodulization of 0.03 to 0.06wt% Magnesium, as well as the addition of Molybdenum, Chromium, Nickel, Copper and Vanadium, although the presence of Niobium is not common. The literature reports that Niobium leads to better mechanical properties of the NCIs, and recent results indicate that 0.5wt% Niobium increases the strength and the Charpy notch toughness of NCIs, but decreases its hardness, in relation to a similar NCI without Niobium. The present report studies the addition of 0.23, 0.47, 0.67, and 0.85wt% Niobium to a NCI covering the effects on the microstructures, yield and tensile strengths, tensile elongations and Charpy toughness. The NCIs were prepared in a 120 kg medium frequency induction furnace, and samples were obtained following the ASTM A842 standard; the various test specimens were extracted from these samples according to specific standards for each test. Fracture analysis was performed in fractures specimens after the Charpy tests. It was shown that the volume fraction of pearlite increases as the Niobium content is raised, leading to increments in the yield and tensile strengths and hardness of these materials. Modest increment of tensile ductility and Charpy toughness are observed only for an addition of 0.23% Niobium. Fracture analysis revealed typical brittle cleavage surfaces and decohesion between grains and grain - graphite nodules interfaces, and very low porosity
Documentos Relacionados
- Microstructural characterization of as-cast hf-b alloys
- Niobium and niobium-iron coatings on API 5LX 70 steel applied with HVOF
- FATIGUE LIFE OF A FERRITIC NODULAR CAST IRON OF DIFFERENT MICROSTRUCTURES.
- Microstructural characterization and mechanical behavior of a low-carbon 17%Mn steel
- Microstructural and mechanical characterisation of the Simon Bolivar's iron bridge structure, 19th century, Arequipa, Peru