Magnetic and structural features of RNi2B2C and RNiBC (R=Er, Ho, Dy, Tb, Gd) superconducting compounds

AUTOR(ES)

Baggio-Saitovitch, E. M., Sánchez, D. R., Micklitz, H.

FONTE

Brazilian Journal of Physics

DATA DE PUBLICAÇÃO

2002-09

RESUMO

Temperature dependent Mössbauer spectroscopy on 57Fe doped (1 at % of Ni) RNi2B2C and RNiBC provided clear evidence of a pair-breaking field at the Ni site for non-superconducting compounds. This field is not present in the superconducting collinear AF DyNi2B2C, however it appears when this compound is diluted with non-magnetic Lu (Dy1-xLu xNi2B2C). Important local information on the spin structure of the R magnetic moments is obtained for both systems. The local symmetries of RNi2B2C and RNiBC compounds, measured through the deltaE Q, were found to be linearly correlated with the c¢/a ratio (c´ is the distance of the R-C layers between which the Ni2-B2 layers are sandwiched). A scaling of Tc with the local symmetry (c¢/a) was found to be the same for all the RNi2B2C and RNiBC (except for Y) compounds.

Documentos Relacionados

• Th e anisotropic magnetocaloric effect in RAl2 (R=Dy, Er, Ho, Nd, Tb) compounds.
• Synthesis of New Isostructural Orthoborates NaBaR(BO3)2 with R = Tb, Dy, Ho, Er, Tm and Lu
• Estudo das propriedades magnéticas e magnetocalóricas em compostos RZn (R= Tb, Gd, Ho e Er)
• Ba2LnSbO6 and Sr2LnSbO6 (Ln = Dy, Ho, Gd) double perovskites: Lanthanides in the geometrically frustrating fcc lattice
• Estudo do efeito magnetocalórico nos sistemas Gd(Al1-xNix)2 e RMg2 (R=Pr, Dy, Er, Nd)