Interrelation Among Morphology, Mechanical Properties and Oxidation Behavior of NbxAlyNz Thin Films

AUTOR(ES)

Carvalho, Renata Gomes

FONTE

Mat. Res.

DATA DE PUBLICAÇÃO

07/11/2019

RESUMO

NbxAlyNz thin films were deposited by magnetron sputtering reactive technique with (y/x+y) ratio varying from 0 to 0.4, in order to maintain aluminum atoms inside NbN matrix in solid solution. GAXRD analyses revealed that the crystalline phase obtained for NbxAlyNz thin films was B1-NbN with a lattice constant shrinkage as Al concentration at these coatings was increased. Due to similarity in electro negativity values between Nb and Al, XPS analyses could not verify pronounced changes among as deposited NbxAlyNz coatings. The average hardness values evidenced that solid solution strengthening mechanism did not increase hardness significantly. The oxidation resistance increased with Al content and no oxide phases were registered by GAXRD analyses for coating with more aluminum added. However, SEM images revealed bubbles after oxidation at high temperatures for all samples.

Documentos Relacionados

• Morphology, structure and mechanical properties of polypropylene modified with organophilic montmorillonite
• Optical Properties and Surface morphology of ZnTe thin films prepared by multiple potential steps
• Structural and Mechanical Properties of Zr-Si-N Thin Films Prepared by Reactive Magnetron Sputtering
• Oxidation Behavior of Al-Y Coating on γ-TiAl at 900°C
• Morphology, microstructure and electrocatalytic properties of activated copper surfaces